The results show that the adsorption capacity and adsorption speed of PACF are higher than that of AC because of its high specific surface area and extensively micropore structure.
结果表明。由于PACF具有高的比表面积和极为发达的微孔结构，因而比AC具有更高的吸附量与吸附速度。
The experiment method of the measurement nanoparticles specific surface areas by the nitrogen adsorption method is investigated.
本文研究了用氮吸附法测定纳米粒子比表面积的实验方法。
The results of TEM and SBET showed that the powder samples possessed higher specific surface area, and it expressed remarkable adsorption properties in methyl orange solution.
用沉淀法合成的粉末样品具有较大的比表面积，并且在甲基橙溶液中表现出了显著的吸附特性。
Silica gels with the high specific surface area and the high adsorption activity have been prepared from water glass and HCL through the process of adding surfactant.
以水玻璃和盐酸为原料，通过添加表面活性剂制备出高比表面、高吸附活性的硅胶。
Sepiolite which is of the highest specific surface area in nature inorganic mineral is used to treat wastewater for its good adsorption capability.
海泡石是目前比表面积最高的天然无机矿物质，由于其良好的吸附特性，用来处理废水有明显的效果。
After modification by organic compounds, the properties of hectorite, such as adsorption abilities, dispersivity and specific surface are improved.
锂皂石有机改性后，吸附性能、分散性及比表面积等提高。
The result shows that adsorption and desorption performance of Benzene vapour by activated carbon are related to the specific surface, hole volume, hole diameter and distribution of hole.
结果表明：苯蒸汽在活性炭上的吸脱附性能明显与吸附剂的比表面、孔容、孔径与孔径分布直接相关。
It shows that the EGME and methylene blue test adsorption methods are well repeating, correct and reliable testing methods of specific surface area.
实验研究证明，EGME法和亚甲基蓝吸附法是重复性好、准确可靠的泥页岩比表面积测定方法。
The CO2-reactivity of char samples fromcoal macerals is related to specific surface area (SN2) measured with N2 adsorption method.
煤岩显微组分富集物焦的CO_2反应性与N_2吸附测得的比表面有关。
Conclusion The Maifanshi adsorption is concerned with specific surface and capillary tube coacervation.
结论：麦饭石的应用与它的表面性质有关且与它的毛细管凝聚作用相关联。
The influence of preparation conditions such as activated temperature and time on yield, specific surface area and adsorption behavior towards n-butane thiol was studied.
研究了聚丙烯腈基活性碳纤维的制备条件，如活化温度、活化时间对产品收率、比表面积及对正丁硫醇吸附与脱除性能的影响。
The specific surface area, pore size and yield ratio have been measured. Iodine and Methylene blue adsorption were used to study the adsorption capacity of ACHF.
测量了比表面积和得率，孔径分布，用碘吸附值、亚甲基兰吸附值测定了中空活性炭纤维的吸附性能，用SEM观察了其表面结构。
The pore size and specific surface area of ACFs were decreased after fluorination. The adsorption isotherm of nitrogen on ACFs were evidently reduced.
氟化后活性炭纤维的孔结构和比表面积变小，氮低温吸附等温曲线明显降低。
This was attributed to the PEG chains present on the surface of complexes that could work as a protective shield layer against aggregation caused by non-specific protein adsorption.
其原因在于存在于合成物表面的PEG链能起到防护层的作用，进而抑制了由于非特异性蛋白质的吸附而引起的聚集反应。
And Aerosil could be used as dispersing agent due to its large specific surface area, high porosity and unique adsorption properties.
由于固体抗粘剂多具有极大的比表面积和空隙率，对难溶性药物有一定的分散作用。
The main factors resulting in the denaturation of encapsulates DGR included the acidic microenvironment and non-specific adsorption of DGR to PLGA surface.
PLGA表面对蛋白质药物的非特异性吸附也会导致部分DGR的失活。
We found that the silicic sol particles formed under microwave radiation have bigger specific surface area and stronger adsorption ability.
通过物理参数的对比测定，得到了在微波辐照下凝聚所产生的硅胶粒子具有更大的表面积和更强的吸附能力。
We found that the silicic sol particles formed under microwave radiation have bigger specific surface area and stronger adsorption ability.
通过物理参数的对比测定，得到了在微波辐照下凝聚所产生的硅胶粒子具有更大的表面积和更强的吸附能力。
应用推荐