The result from point scanning and surface scanning analysis on both sides and body of sample ZJ1 pointed out that the coin moulds were used for casting bronze coin.
钱范ZJ1的正、反面和胎的点扫描和面扫描分析结果表明，其应为铸造铜钱之范。
Analysis is made on the dark lines defects occurring over the working surface of flange by measurement with the optical microscope, Scanning electro microscope (SEM) and electronic probe.
针对法兰盘加工面上出现的黑纹缺陷，采用光学显微镜、扫描电镜和电子探针等测试方法对其进行了分析。
The causes of the front fog lamp shield blistering after surface treatment are studied by means of metalloscopy scanning electronic microscope and energy spectrum analysis.
运用金相显微镜、描电镜和能谱仪，研究了前雾灯遮光罩表面处理后起泡的原因。
The failure analysis consisted of a strength analysis, a macro-fracture surface analysis, a metallurgical microscope and scanning electron microscope analysis.
分析包括结构强度分析、宏观断口分析、金相分析和扫描电镜分析等。
Using X-ray diffraction, energy spectrum analysis and scanning electron microscope, TiO2 crystallite, shape and size on ceramic surface are tested.
利用x射线衍射仪、能谱分析和电子扫描电镜对瓷砖釉面表面的二氧化钛晶型、形貌、颗粒大小进行了测试。
The effect of residual elements on the continuous cast slabs and surface quality of hot rolled plates is studied by scanning electron microscope, transmission electron microscope and EDS analysis.
通过扫描电镜、透射电镜和EDS分析，对残余元素对连铸坯和热轧板表面质量的影响进行了研究。
The open circuit potential, potentiodynamic scanning polarization and surface analysis methods were employed to investigate the effect of Cladosporium on the corrosion behaviors of A3 steel.
采用开路电位法、动电位扫描法和表面分析法研究了油-水体系中枝孢霉菌对A3钢电化学行为的影响。
The surface defect on medium and heavy plate Q235B was investigated by means of the optical microscopy, scanning electron microscopy and energy spectrum analysis in this paper.
对Q 235 B中厚板表面缺陷处的显微组织、非金属夹杂物等进行了金相组织和扫描电镜观察及能谱分析。
In addition, the surface topography and element distribution were analyzed by Scanning electrical microscope (SEM) and Energy dispersive X-ray analysis (EDS) as well.
同时采用SEM和EDS对磨斑表面形貌和元素的面分布进了研究。
In addition, the surface topography and element distribution were analyzed by Scanning electrical microscope (SEM) and Energy dispersive X-ray analysis (EDS) as well.
同时采用SEM和EDS对磨斑表面形貌和元素的面分布进了研究。