Most precipitate dissolve into the matrix after solution treatment.
材料经固溶处理后析出物绝大多数都溶入基体。
The results show that there are lots of uneven ordering domain after solution treatment.
结果发现，其固溶态含有大量有序畴的不均匀固溶体；
Grain growth exponent increases with the increasing of solid solution treatment temperature.
晶粒生长指数随固溶温度的升高而增加。
It is important to control the forging temperature and solution treatment temperature lower rather than higher.
重要的是较低的锻造温度和热处理固溶温度比较高的好得多。
In the case of solution treatment adequately, the variation of wall thickness almost haven't any effect on aging.
在充分固溶的情况下，壁厚不同对时效影响不大。
The alloys in plastic after solution treatment good, easy Rolling and Processing of the various parts of complex shape;
该合金在固溶处理后塑性良好，易于辗压及加工成型各种形状复杂的零件；
The influence to corrosion resistant ability of duplex stainless steel (SAF2205) after solution treatment to weld joint.
分析了采用焊后固溶处理对SAF2205双相不锈钢耐腐蚀性能的影响。
And solution treatment is the valid method to improve the anticorrosion property of the austenite stainless steel bellows.
固溶处理是改善和提高奥氏体不锈钢波纹管抗应力腐蚀能力的有效措施。
This paper deals with the low frequency damping of ZA27 alloy with solid solution treatment after natural ageing stability.
研究了固溶化处理的ZA2 7合金在自然时效稳定后的低频阻尼。
The effects of progressive solution treatment on microstructure and mechanical properties of 7A04 aluminum alloy were investigated.
研究了分级固溶对7A04铝合金组织与性能的影响。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
Intermetallic compound foam reinforced aluminium alloy surface composite layer are obtained by solution treatment after low pressure Casting.
通过低压铸造后固溶处理的方法，获得了网状金属间化合物增强铝合金表面复合层。
The precipitation behavior of sillicide in BT25y high temperature titanium alloy under solution treatment and thermal exposure was observed with TEM.
介绍了高聚物合金钛涂料的制备特点、主要成份与理化性能，以及该涂料的施工方法和应用结果。
The influence of different solid solution treatment on the structure and corrosion resistant property of cast duplex stainless steel was investigated.
研究了不同固溶处理对双相铸造不锈钢的组织及其耐蚀性能的影响。
After solution treatment, the weld grains become coarse along with a large amount of granular precipitates dispersed in weld zone and base metal zones.
经过固溶处理后，焊缝组织晶粒变大，焊缝区和母材区弥散分布着大量的颗粒状析出物。
Flow injection technique is a solution treatment technique under nonhomogeneous and unbalanced condition and has gained wide application in food analysis.
流动注射是一种非均匀非平衡状态下的溶液处理技术，在食品分析领域中的应用日益广泛。
By proper solution treatment the grain size of alloys was moderate, thus a good combination of strength, plasticity and the resistance to thermal fatigue was obtained.
采用适当固溶温度处理，该二合金晶粒度适中，可获得强度、塑性和抗热疲劳性能较好的配合。
The effect of high temperature solution treatment on the structure and properties of a directionally solidified high strength nickel-base superalloy has been investigated.
本文研究高温固溶处理对一种定向凝固高强度镍基高温合金的组织和性能的影响。
Effects of master alloy of quasicrystal containing magnesium additions and solution treatment on microstructure and mechanical properties of AZ91 magnesium alloy were studied.
研究了镁基准晶中间合金和固溶处理工艺对AZ91合金显微组织和力学性能的影响。
It includes the effect of manganese content, solution treatment temperature and cooling rate on the non equilibrium segregation of manganese and condition of segregation formation.
研究了锰的质量分数、固溶处理温度和淬火冷却速度对锰不平衡偏聚的影响和不形成锰偏聚的条件。
The device has these features that temperature acquisition, accurate heating time, timely cooling etc; it provides the high level automation device to steel U-tube solution treatment.
装置具有温度采集、加热时间准确、及时冷却等优点，为不锈钢u形管固溶处理提供了自动化水平比较高的设备。
The results show that the electrochemical performance of aluminum alloy electrodes is improved markedly after solution treatment, but the self-corrupt speed of electrodes is accelerated.
结果表明，经过固熔处理后，铝合金电极的电化学活性得到显著提高，但自腐蚀速率加快。
The results showed that calcium solution treatment significantly increased total calcium content in fruits, improved fruit firmness and maintained permeability of cell membrane significantly.
结果表明：浸钙处理的果实总钙含量显著提高，其硬度明显高于对照，且有利于细胞膜透性的保持；
The result showed that copper was distributed inharmoniously in the supersaturation ferrite after solution treatment, in which a large number of namostructure ordering domain was distributed.
这种过饱和铁素体基体上分布着大量纳米级的有序畴结构。
The results show that the suitable solution treatment process can reduce the size and amount of coarse second phases effectively and then increase the super-saturation degree of alloy elements.
结果表明：利用优化的固溶工艺处理后，可有效减少粗大的第二相尺寸和数量，提高合金元素的固溶过饱和度；
The temperature of solid solution treatment affected not only the degree of the second phase dissolved in the matrix alloy, but also the recovery and recrystallization processing level of the alloy.
固溶处理温度的高低不仅影响第二相在基体中的溶解程度，还影响合金的回复再结晶过程进行的程度。
The results show that the precipitated austenite crystals of welded joint after solid solution treatment are fewer, the grains are smaller. And the shape of austenite changes from strip to roundness.
结果表明：经固溶处理的焊缝和热影响区，晶内奥氏体析出变少，晶粒尺寸变小，同时奥氏体的形状由长条状变为圆状。
The results show that the precipitated austenite crystals of welded joint after solid solution treatment are fewer, the grains are smaller. And the shape of austenite changes from strip to roundness.
结果表明：经固溶处理的焊缝和热影响区，晶内奥氏体析出变少，晶粒尺寸变小，同时奥氏体的形状由长条状变为圆状。