The porosity gradient of porous aluminium is mostly affected not only by the spontaneous stacking density of granules, but also by the infiltration pressure gradient and solidification sequence.
多孔铝合金的孔隙率梯度主要是由渗流驱动压力梯度与凝固顺序所决定，而颗粒的自然堆积密度影响相对较小。
It is discussed that adiabatic material, as well as ratio of height and width effected solidification, shrinkage cavity and shrinkage porosity.
讨论了锭模的高宽比、绝热板材质对凝固位置及缩孔疏松的影响。
The results indicate that the casting defects are mainly shrinkage porosity and cracks caused by solidification shrink, which mainly presents in the hot spot between the spoke and the rim.
研究表明：轮毂的工艺缺陷主要为缩孔、缩松以及凝固过程中收缩导致的裂纹缺陷，主要分布在轮辋、辐条交汇的热节部位。
The results indicate that the casting defects are mainly shrinkage porosity and cracks caused by solidification shrink, which mainly presents in the hot spot between the spoke and the rim.
研究表明：轮毂的工艺缺陷主要为缩孔、缩松以及凝固过程中收缩导致的裂纹缺陷，主要分布在轮辋、辐条交汇的热节部位。