The failure mechanism of a roll shell in continuous roll casting is discussed and a formula for predicting its fatigue life is established.
分析了铸轧辊套的失效机理；提出了铸轧辊套疲劳寿命预报公式。
It is found that the distribution of temperature field in roll shell is just like a stress field following Saint-Venant principle in elastic mechanics.
发现辊套温度场分布规律与弹性力学中的应力场分布遵循圣维南原理相似。
Result showed that main reasons on ablation of roll bearing were transformation of forward Angle, flow value of cool water, water pressure, water pipe position, and deformation of roll-shell et al.
对造成轧辊烧轴承的原因进行了分析，结果表明：轧辊烧轴承主要与轧辊送进角的变化，冷却水的水量、水压及水管位置，轧辊架变形情况等有关。
Result showed that main reasons on ablation of roll bearing were transformation of forward Angle, flow value of cool water, water pressure, water pipe position, and deformation of roll-shell et al.
对造成轧辊烧轴承的原因进行了分析，结果表明：轧辊烧轴承主要与轧辊送进角的变化，冷却水的水量、水压及水管位置，轧辊架变形情况等有关。