Rod should not have obvious camber, crack, burr, peeling or other defect affecting he further USES.
杆料不应有明显弯曲，裂缝、毛刺、起皮及影响使用的其他缺陷。
Aemission spectrometer, micro-hardometer, optical microscope and scanning electron microscope were used to analyze the reason of crack on connecting rod unit assembly for piston of car engine.
采用直读光谱仪、显微硬度机、光学显微镜和扫描电子显微镜等分析手段，对失效的汽车发动机活塞连杆总成断裂原因进行了分析。
For the inner crack appearing often in round-rod rolling steels in the production, the influence to the crack from deformation extent and mechanical condition in the deformation region is discussed.
圆棒轧材在生产过程中经常出现内裂纹，本文研究了变形程度和变形区力学条件对内裂纹的影响。
The result has shown that the fracture was caused by such surface defects as fold crack in section a at connecting rod small end.
结果表明，断裂由连杆小头A截面的表面缺陷(折叠裂纹等)引起。
But whether high chrome cast iron welding rod produces more crack in the overlaying process is with the relation of more horniness carbonization in its organization.
而高铬铸铁型焊条，在堆焊过程中出现较多裂纹，与其组织中有较多的硬质碳化物有关。
But whether high chrome cast iron welding rod produces more crack in the overlaying process is with the relation of more horniness carbonization in its organization.
而高铬铸铁型焊条，在堆焊过程中出现较多裂纹，与其组织中有较多的硬质碳化物有关。