A resin system is composed of resins, curing agents and accelerants.
树脂与固化剂、促进剂等混合后组成树脂体系。
Specially make the focal point on high reactive phenolic resin system.
重点论述了高反应活性的树脂系统。
The results show that AD appears to be a latent accelerator for the anhydride-cured epoxy resin system.
结果表明，乙酰丙酮钕对体系的固化具有潜伏性促进作用。
The relations of viscosity vs. temperature and gel time vs. temperature of 3233 epoxy resin system are studied.
研究了3233环氧树脂体系的粘度-温度关系、凝胶时间-温度关系、热力学性能、垂直燃烧性能和力学性能。
The results show that polyetherimide can not only toughen this resin system, but improve the dielectric performance.
研究表明，聚醚酰亚胺在改善氰酸酯树脂体系韧性的同时，也提高了树脂体系的介电性能。
Can be used as base metal coating materials used vinyl resin system by plastisol or solution, polyester or acrylic, etc.
可以作为金属涂布的底基材料使用的树脂系统有乙烯、聚酯或丙烯酸等。
The title coatings has been prepared by use of melting intercalation technology to introduce the OMMT into epoxy resin system.
利用熔融插层法将有机蒙脱土引入环氧树脂体系，制备出含有纳米分散蒙脱土的无溶剂环氧涂料。
The suitable processing parameters used in RTM processing is determined base on the study of resin system processing properties.
通过对树脂体系的工艺特性研究，确定了其用于RTM工艺的最佳工艺参数。
We can offer the right resin system for your application as well as all of the instrumentation and accessories to fit your needs.
我们会根据您的要求，选择适当的树脂系统、装置和附件。
The unidirectional aramid reinforced composite made of the resin system and the aramid fibre has excellent mechanical properties.
用该树脂体系与芳纶纤维制成的单向复合材料(缩写为KFRP)具有优异的力学性能。
Heat resistance, curing reaction, and morphology of the modified phenolic resin system were characterized by TG, DSC, SEM and tem.
借助TG、DSC、SEM和TEM对改性酚醛树脂体系的耐热性能、固化反应和微观形态进行了表征。
The properties of the resins, the cured resins, and composites have been studied. A good properties resin system has been obtained.
对其树脂、固化树脂及其复合材料的性能进行了详细的研究，得到了性能较佳的树脂体系。
The results show that the addition of PET resin extends gel time, narrows temperature range at low viscosity of the melt resin system.
研究结果表明：PEI的加入使树脂体系的凝胶时间延长，导致树脂熔液在低粘度时的温度范围缩小和粘度增大。
SEM analysis indicated that there was remarkable toughness fracture surface morphology for the epoxy resin system modified with ESBSVP.
SEM结果表明，经ESBSVP改性的环氧树脂体系断面呈现出明显的韧性断裂特征。
From the design of epoxy resin system, two-stage rigidization epoxy resin matrix with thermal induced shape memory property was prepared.
本文制备了可二阶段固化的形状记忆环氧树脂基体，研究了形状记忆环氧树脂及其复合材料的形状记忆特性和力学性能。
The cure kinetics of bismaleimides (BMI) resin system was investigated by dynamic DSC analysis and the phenomenological model was established.
采用全动态dsc研究了双马来酰亚胺树脂(BMI)体系的固化反应动力学，建立了固化动力学的唯象模型。
The resin system applicable for the equipment includes epoxy, phenolic, polyurethane and other two-component or single-component resin system.
该设备适用的树脂体系包括环氧、酚醛、聚氨酯等双组分或单组分树脂体系。
Based on analyzing the curing characteristics of the resin system and the isothermal viscosity curves, an engineering viscosity model was developed.
根据对树脂固化特性和等温粘度曲线的分析，建立了树脂体系的工程粘度模型。
The choice of this paper is the epoxy resin and polyethylene polyamine curing system, and glass fiber reinforced epoxy resin system as the damping materials.
本文选择的是环氧树脂和多乙烯多胺固化体系，以及玻璃纤维增强环氧树脂体系作为阻尼层材料。
The dielectric performance of the modified resin system is remarkably influenced by the concentration of catalysis, the cure temperature and toughening agent.
树脂的介电性能与树脂体系的催化剂含量、固化温度和增韧剂含量有较大关系。
The cyanate resin is modificated by styrene and divinyl benzene, which are called active diluent. The modificated resin system has low viscosity and store stability.
以苯乙烯和二乙烯基苯作为氰酸酯树脂的活性稀释剂，得到粘度低、贮存稳定性好的改性树脂体系。
The latent curing acceleration of the rareearth organometallic compound (MrAn) for the anhydride/epoxy resin system was studied by DSC, TG and rotation viscometer, etc.
结果表明，这种稀土化合物是酸酐／环氧树脂体系较为理想的潜伏性促进剂。
The results showed that the fracture surface of the modified systems displayed tough fracture features, markedly different from that of the unmodified epoxy resin system.
结果表明，增韧后材料的断面形态明显不同于未改性体系的形态，试样冲击断裂面形态具有明显的韧性断裂特征。
This article has reviewed the development and progress of waterborne epoxy resin system at home and abroad, and described its preparation approaches and application fields.
总结了目前国内外水性环氧树脂体系的研究进展，并介绍了水性环氧涂料的制备方法与应用领域。
A new type UP resin system curing at room temperature was introduced as well as the influence of various initiators, promoters on the gel, curing and photic rate of the system.
介绍不饱和聚酯树脂新型室温固化体系，以及不同引发剂、促进剂对体系凝胶、固化和透光率的影响。
The distilled water resistance of this system is better than low molecular weight polyamide cured epoxy resin system. This is proved by macroscopic examination and microcosmic AFM analysis.
通过宏观试验和AFM微观分析证明，改性酚醛胺固化环氧树脂体系的耐蒸馏水性能，优于低分子聚酰胺固化的环氧树脂体系。
The viscosity and gel time of resin system of modified bismaleimide(BMI) resin with rigid polyetherimide(PEI) and the mechanical properties of PEI/BMI/RS/ glass composite materials were studied.
研究了刚性聚醚酰亚胺（PEI）改性双马来酰亚胺（BMI）树脂体系粘度特性和凝胶特性，以及PEI/BMI/RS/玻纤复合材料的力学性能。
The viscosity and gel time of resin system of modified bismaleimide(BMI) resin with rigid polyetherimide(PEI) and the mechanical properties of PEI/BMI/RS/ glass composite materials were studied.
研究了刚性聚醚酰亚胺（PEI）改性双马来酰亚胺（BMI）树脂体系粘度特性和凝胶特性，以及PEI/BMI/RS/玻纤复合材料的力学性能。