The experimental results showed that in the annealing condition the recrystallization texture has an important influence on the capacitance of etched al foil.
实验表明：在退火条件下，再结晶织构对腐蚀铝箔的电容量有重要影响。
The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.
采用晶体取向分布函数（ODF）、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。
The effect of electric field on the recrystallization and recrystallization texture development in cold-rolled copper was studied by X-ray diffraction (ODF analysis) combined with optical microscopy.
利用X射线衍射技术并结合金相组织观察和显微硬度实验，研究了冷轧工业纯钢在电场作用下的再结晶及织构演变规律。
High finish rolling temperature promotes the recrystallization of hot-rolled strip, increases favorable texture components, decreases the core loss, and increases magnetic induction of final product.
提高终轧温度可以促进热轧板的再结晶，增加成品中有利织构组分，降低铁损，提高磁感。
It is found that cube texture in this alloy can be developed either by the process of secondary recrystallization or simply by the process of primary recrystallization.
通过二次再结晶形成立方织构时，并不包括重新形核的过程。
Recrystallization is the necessary condition for spheroidization of the deformed texture.
再结晶是形变组织球化过程的必要条件。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。