This difficulty can be solved by flexible co-woven prepreg technology, facilitating the manufacture of complex curved surface structure with high quality and efficiency.
利用柔性混编预浸料技术则可解决这一难题，高质量、高效率地实现复杂曲面结构件的制备。
The hybrid prepreg substrate (32) is coupled to the base substrate (30).
所述预浸渍基材（32）耦接到所述基体基材（30）。
ACG Group is one of the most famous companies producing prepreg and composite materials in the world.
先进复合材料集团公司是世界上生产预浸料和复合材料最有名的公司之一。
For the volatile content, the prepreg made by the hot-melt method was lower, generally less than 0.8%.
在预浸料挥发分方面，热熔法工艺的较低，一般低于0.8%。
Using this device and the method of this invention can improve the width prepreg soakage property greatly.
利用本发明的装置和方法可大大改善宽幅预浸料浸润性。
In this paper, the technology of carbon fiber reinforced PEEK prepreg produced by melt impregnation is investigated.
初步探索了熔融浸渍法制备碳纤维增强PEEK预浸带的制备工艺。
Good prepreg with stable processing and according with demands can be fabricated by controlling these factors reasonably.
通过合理控制这些影响因素，可制备出工艺状态稳定、质量符合要求的预浸无纬布。
The polyimide resin is suitable for steeping carbon fiber, fiber glass or aramid fiber and the like to be prepared into prepreg;
所述的聚酰亚胺树脂适于浸渍碳纤 维、玻璃纤维或芳纶纤维等，制成预浸料；
The stitching process was applied to improve the properties in the throughthickness direction of composites based on prepreg materials.
采用缝纫工艺对基于预浸料辅层的复合材料进行厚度方向增强，用落球法进行了冲击损伤和冲击后压缩破坏实验。
And the increasing of prepreg tack can significantly improve the lateral bending performance, which all agree with theoretical prediction well.
增加预浸料黏附力可显著提高其侧向弯曲性能，符合理论分析结果。
The resin blend has been heated to a temperature substantially greater than 225 degrees Celsius in a curing process when preparing the prepreg.
当制备该半固化片时，所述树脂掺合物在固化程序中经加热至实质上高于摄氏225度的温度。
Microcapsule-type curing agent, method for producing the same, thermosetting resin composition, prepreg and fiber reinforced composite material.
微胶囊型固化剂，其制备方法，热固性树脂组合物，预浸渍物及纤维增强的复合材料。
The properties of plain carbon fabric prepreg were researched using a picture frame shear rig which is (installed) on a mechanical test machine.
利用安装在拉伸试验机上的像框剪切装置，研究了平纹预浸碳纤维机织织物的剪切行为。
The experiment results show that ultrasonic cutting technique is an effective, clean and controllable method for machining of carbon fibre prepreg. $
实验结果表明，对于纤维预浸料的切割与下料，超声切割技术是一种可获得高质量、高效率的加工方法。
Tests were also carried out in composite manufacture, in which the fiber optic refractive sensors were embedded in the prepreg during the cure process.
在实验室与生产现场两种条件下将光纤折射率传感器埋设于预浸料中对其固化工艺过程进行了监测。
This kind of equipment is suitable for produce hot-melt prepreg composite materials by two-step. It includes hot-melt sizing machine and prepreg machine.
我公司生产的预浸设备为二步法生产热熔预浸复合材料设备，主要包括热熔涂胶机和热熔预浸机。
The prepreg cloth is generally of sandwich structure with release paper or plastic film on both sides and carbon fiber or glass fiber prepreg in the center.
预浸布均为夹层结构，两面是离型纸或者塑料膜，中间夹芯为碳纤维或玻璃纤维预浸材料。
The prepreg hot pressing condition is optimized by analyzing TGA and studying influence of parameters on dielectric and mechanical properties of composites.
通过热失重TGA分析以及考察加工成型过程中工艺参数变化对复合材料介电性能、力学性能的影响 ，优化了预浸料热压成型工艺条件。
The testing method and standardization of carbon fiber and its fabric, prepreg, CFRP are illustrated both at home and abroad, for some testing units reference.
论述了国内外碳纤维及其织物、预浸料、 复合材料的测试方法及标准化，供国内有关测试单位及专业技术人员参考。
A new matrix resin for composite 4501b is introduced, the properties of the resin, cured resin and composites are studied, and the processability of the prepreg is also shown.
本文介绍一种新的复合材料用树脂基体4501b，研究了树脂的性能、固化树脂的性能、预浸料的工艺性及复合材料的性能等。
The resin content, the volatile content and the pre-curing degree of the silica/phenolic resin prepreg cloth were on-line determined by near infrared diffuse reflection spectrum.
采用近红外漫反射光谱技术对高硅氧/酚醛预浸布的树脂含量、挥发分含量和预固化度等质量指标进行了在线测定。
A method of forming an exterior surface protective structure (12) for an aircraft (10) includes uniting a loaded surfacer (52) having a carrier (51) to a hybrid prepreg substrate (32).
一种为飞行器(10)形成外部表面防护结构(12)的方法，包括将具有载体(51)的受载表面料(52)结合到混合预浸渍基材(32)。
In the process of producing continuous fiber reinforced PEEK prepreg with the melt impregnation method, the fiber bundles are required to be well pre-dispersed to acquire good impregnated prepreg.
熔融浸渍工艺制备连续纤维增强peek预浸带，要求纤维束必须预分散以获得浸渍效果较好的预浸带。
By analyzing the power transfer between the infrared heat source and the prepreg, the paper proposes calculation methods and equations about the transfer coefficients in the infrared heating process.
通过对红外热源与预浸带能量传输过程的分析，提出了红外加热过程中各传递系数的计算方法和公式。
The impregnating methods concerned in this paper have the advantages such as availability for different types of resin systems, prepreg with uniform resin content and higher producing efficiency, etc.
本文所涉及的预浸方法具有如下优点：适于不同体系的树脂，预浸料树脂含量均匀，生产效率高等。
Using Imported Prepreg as the Raw Material, the Second Overall Compression Molding for External Trough Line and the Tube, Excellent Surface Finishment and Mechanical Performance.
采用进口预浸布作为原材料，槽线与管体二次固化整体成型，表面光洁度和力学性能优异。
Using Imported Prepreg as the Raw Material, the Second Overall Compression Molding for External Trough Line and the Tube, Excellent Surface Finishment and Mechanical Performance.
采用进口预浸布作为原材料，槽线与管体二次固化整体成型，表面光洁度和力学性能优异。