Residual compression ACTS on the plastic deformation layer.
残余压应力作用在塑性变形层内。
When abrasive grains impacted on the work piece surface, the top layer atomics are removed, plastic deformation appears at the same time.
纳米级的磨粒冲击到工件表面，在以原子级去除的同时伴随着塑性变形的发生。
The advantage of this method consists in the fact that neither a protective layer nor creep properties are necessary and that question about clastic or plastic deformation can be avoided.
它的优点在于不必给试样单面施加抗氧化涂层，不需要研究材料的蠕变性质，也不必讨论试样的形变属于弹性形变还是属于塑性形变。
This paper advanced a study method that can observe plastic deformation behavior of surface layer of die cavity by showing austenite grain, size, crack morphology and propagation mode.
提出了通过显示奥氏体实际晶粒度、裂纹形貌和扩展方式来分析热锻模具型腔表层塑性变形行为的试验方法。
The larger the plastic deformation of the buffer layer, the higher the joint strength.
缓冲层塑性变形愈大，接头强度愈高。
The severe plastic deformation is the main mechanism of white layer formation during precision hard part machining process.
精密硬态切削表面白层的形成是剧烈塑性变形导致的。
The result indicates that the improvement of the fatigue limit is due to the nano-crystallization and severe plastic deformation in the surface layer induced by high-energy shot peening.
结果表明，高能喷丸后其表层组织发生严重塑性变形并实现组织纳米化，是提高弯曲疲劳寿命的主要原因。
The results showed that the formation mechanism of the white layer is strong plastic deformation.
结果表明，白层形成机制为强烈塑性变形机制。
All these results show that severe plastic deformation occurred on the grinding surface, the strain strengthening is the basic reason for the increase of the yield strength in grinding affected layer.
这些结果说明，磨削表面发生了严重的塑性形变。冷作塑性形变强化是磨削影响层的屈服强度得以提高的根本原因。
The use of plasticized rosin as an analog material of the ductile lower lithosphere provides an effective approach to modelling intraplate plastic flow network and multi layer tectonic deformation.
采用塑化松香作为岩石圈延性下层的相似材料，进行了板内塑性流动网络及多层构造变形的物理模拟实验。
Preferably, the high crystallinity layer is capable of undergoing plastic deformation upon the elongation.
优选地，该高结晶度层在伸长时可经历塑性形变。
Preferably, the high crystallinity layer is capable of undergoing plastic deformation upon the elongation.
优选地，该高结晶度层在伸长时可经历塑性形变。