The effect of speed ratio on the texture of non-oriented cold rolled low silicon steel sheet was investigated after cross shear rolling at different speed ratios.
选取低硅无取向硅钢常化态板材，分别在不同速比下进行异步轧制，考察了速比对低硅无取向硅钢冷轧织构的影响。
The results show that the grain size of cold-rolled non-oriented silicon steel finished product decreases and benefiting texture component increases with increasing slab reheating temperature.
结果表明，随着铸坯加热温度的提高，冷轧无取向硅钢成品晶粒尺寸减少，有利织构组分增加。
The relationship between the different direction magnetic properties (B8), texture and the magneto-crystalline anisotropy energy (EK) of a doubly oriented Si steel has been investigated.
研究了一种双取向硅钢不同方向的磁感(B8)及其与织构和磁晶各向异性能(EK)之间的关系。
The results show that using high and low slab reheating temperature technique, the texture component of hot rolled grain oriented silicon steel is significantly different from that of cold rolled one.
采用取向分布函数及取向线分析方法对取向硅钢高温和低温板坯加热工艺的热轧及冷轧钢板织构进行了研究。
The calculation of single crystal magnetic induction coefficients from measured texture and magnetic induction data in a grain-oriented silicon steel strip has been discussed.
对由取向硅钢薄带的磁感和织构实测数据计算其单晶磁感系数进行了探讨。
The effect of normalizing temperature on microstructure and texture of non-oriented silicon steel sheets when adopting double cold reduction has been studied.
研究了二次冷轧工艺常化温度对冷轧无取向硅钢薄带组织结构和磁性能的影响。
The variation of the texture and magnetic properties of non-oriented silicon steel after being cold-rolled and annealed is studied.
对冷轧及退火后无取向硅钢织构及磁性能的变化进行研究。
Compared with pure hydrogen atmosphere, decomposed ammonia atmosphere is more propitious to the formation of advantaged texture of non-oriented silicon steel.
同全氢气氛相比较，氨分解气氛更有利于50aw 600无取向硅钢有利织构的形成。
Compared with pure hydrogen atmosphere, decomposed ammonia atmosphere is more propitious to the formation of advantaged texture of non-oriented silicon steel.
同全氢气氛相比较，氨分解气氛更有利于50aw 600无取向硅钢有利织构的形成。