The results showed that the fracture was of typical fatigue fracture, and surface defects were the main factor resulting in the failure of the air valve spring.
结果表明，断裂呈现典型的疲劳断裂特征，材料表面缺陷是引起该弹簧疲劳断裂的主要原因。
The results showed that the fracture was of typical fatigue fracture, and surface defects were the main factor resulting in the failure of the air valve spring.
结果表明，断裂呈现典型的疲劳断裂特征，材料表面缺陷是引起该弹簧疲劳断裂的主要原因。