The results showed that the immanent quality disfigurement of billets, the heating temperature on the high side and non-uniform were the main factors to cause the edge cracking.
结果表明，钢坯的内在缺陷、加热温度偏高及加热不均匀是产生边裂的主要原因。
The results showed that the immanent quality disfigurement of billets, the heating temperature on the high side and non-uniform were the main factors to cause the edge cracking.
结果表明，钢坯的内在缺陷、加热温度偏高及加热不均匀是产生边裂的主要原因。