This paper discusses the effect of brazing time, brazing temperature, brazing gap and diffusion treatment on the remelt temperature of the brazed joint.
文章讨论了钎焊时间、钎焊温度、钎焊间隙及焊后扩散处理对钎焊接头再熔化温度的影响。
The results show that the interface between nickel solder and steel is metallurgical joint by diffusion.
研究结果表明，镍基钎焊层通过扩散形成界面，实现了完全的冶金结合。
The direct bonding joint between cemented carbide and nodular cast iron and the indirect bonding joint by using nickel foil as intermediate layer were obtained by HIP diffusion bonding process.
用热等静压扩散连接法获得了硬质合金与球墨铸铁的直接连接接头和以镍箔为中间夹层的间接连接接头。
The microstructure, element diffusion and appearance of joint were analysed.
分析了接头微观组织结构，元素的扩散及断口形貌。
The dynamic behavior of hydrogen in this joint was observed by photographing under the microscope, the diffusion behavior and the escaping course of hydrogen was definited.
在微观上应用显微镜下录象测氢试验法观测焊接接头中氢的动态行为，明确了氢的微观扩散行为及逸出过程。
The experimental data were fitted to a mathematical model of joint controlled by the chemical reaction at the interface and diffusion of steam through the product layer.
实验数据与界面化学反应和固体产物层内扩散共同控制数学模型相吻合。
The microforms of diffusion joint were analyzed using field emission scanning electron microscope with an attached energy dispersive Xray analyzer.
利用场发射电镜、能谱仪等对接合区的界面和组织形貌进行了分析比较。
Plastic deformation conditions have great influence on the diffusion bonded joint, but there was little knowledge about its rule.
扩散焊焊接中的塑性变形条件对接头性能有很大影响，目前对其影响规律缺乏系统认识。
Plastic deformation conditions have great influence on the diffusion bonded joint, but there was little knowledge about its rule.
扩散焊焊接中的塑性变形条件对接头性能有很大影响，目前对其影响规律缺乏系统认识。