The research indicate that (1) when the specific gravity and modulus of soluble glass is 1.5 and 1.1, the effect of activate slag is best.
试验研究表明：(1)水玻璃在比重和模数分别为1.5和1.1时，对矿渣激发的效果最好。
The effect of various factors shrinkage property of slag based geopolymer concrete are studied by shrinkage test, such as content and modulus of water glass, liquid-solid ratio, gel material content.
通过混凝土收缩试验，研究了水玻璃掺量、水玻璃模数、液固比、胶凝材料用量等因素对无机矿物聚合物混凝土收缩性能的影响。
The results show that shrinkage of concrete firstly decreases and then increases , with the increase of modulus of water glass.
研究结果表明，随着水玻璃模数的增加，无机矿物聚合物混凝土的收缩呈现先降低后增加的趋势；
Dynamic mechanical thermal analysis showed that the addition of TPR improved the damping of the composite, but decreased the storage modulus and the glass transition temperature of the composite.
复合材料动态力学性能研究表明：TPR的加入提高了复合材料的阻尼性质，却降低了复合材料的存储模量和玻璃化转变温度；
The plastic fiber selected has different ultimate tensile strain and elastic modulus, and the fiber can be carbon fiber, aramid fiber, glass fiber and the like.
选用的塑料纤维应具有不同的极限拉应变和弹性模量，纤维可以为碳纤维、芳纶纤维、玻璃纤维等。
A main body of adopted raw materials is tows of high-performance fiber such as fiber glass, carbon fiber, aramid fiber, ultra high modulus polyethylene and the like.
采用的原料主体为玻璃纤维、碳纤维、芳纶纤维、超高模量聚乙烯等高性能纤维丝束。
The results showed that the storage modulus of PP was increased markedly and the glass transition temperature of PP was risen by the addition of the nucleating agents.
结果表明：有机磷酸酯成核剂使PP的储能模量显著提高，玻璃化转变温度有所增加。
The tensile strength and elastic modulus of glass fiber reinforced plastic(GFRP), which was made by different layers of glass fiber fabric, were tested and analyzed.
测试了不同层数玻纤布制成的玻璃钢拉伸强度和弹性模量。
The toughness of epoxy resin is appreciably enhanced by adding some PES, in the meantime, the modulus and glass transition tempeerature, Tg, of epoxy resin are not decreased but increased. Th…
加入一定量PES可较大幅度地提高环氧树脂的韧性，而不降低环氧树脂的模量和耐热性。
Composites with well general mechanical properties, such as unchanged tensile strength and modulus and higher impact strength were obtained by adopting technologies of polyolefin and glass-fiber.
采用聚烯烃增韧与玻璃纤维共混，在保持复合材料拉伸强度和模量的同时，较大地提高了冲击强度，获得了综合力学性能优异的纤维增强聚酰胺材料。
Automotive interiors. 10% glass-reinforced. Increased stiffness/structural rigidity. High modulus/ductile. Foamed skin instrument panel uses also.
汽车内部件。10% 玻璃纤维增强。改良的劲度、结构刚度。高模量、高延性。也可用于泡沫塑料面层仪表板。
The test results showed that the activation effect of low-modulus water glass is optimal.
实验表明，低模数水玻璃对三种废渣的激发效果最好。
The test results showed that the activation effect of low-modulus water glass is optimal.
实验表明，低模数水玻璃对三种废渣的激发效果最好。