Fractographic observations showed that hydrogen could induce surface cracks for smooth specimens and a cleavage fracture pattern for notch specimens at RT.
破断面观察结果显示，在室温中，氢气会导致平滑试片在表面形成裂纹，而在凹槽试片中产生劈裂破坏形态。