The equilibrium eutectic temperature is calculated for solidification of gray, ductile and white iron.
灰铁、球铁及白铁凝固时即为平衡共晶温度。
The eutectic temperature and eutectic point of Momordica charantia juice were measured by using a simple apparatus.
为了对苦瓜汁进行真空冷冻干燥，首先通过简单的电阻装置测定了苦瓜汁的共晶点与共融点。
The results show that: manganese lowers liquidus and eutectic temperature, and narrows down the temperature range of solidification;
结果表明：锰降低液相线温度和共晶温度，缩小凝固温度范围；
All graphitizing elements decrease the metastable eutectic temperature, increase the stable eutectic temperature and enlarge their distance.
所有石墨化元素均降低介稳定共晶温度，而提高稳定共晶温度，并使两者间距扩大。
"Eutectic" refers to a mix of elements or compound that remains liquid at lower temperature than either of its components does alone.
“共晶”是指一种元素或者化合物的组合，它可以在比任一成分单独时的凝固点更低的温度下保持液态。
In the first stage (large heating sublimation stage), product temperature lower than the eutectic point of a range.
在升温的第一阶段(大量升华阶段)，制品温度要低于其共晶点一个范围。
Experience proves, supercooling phenomenon is easy to occur to make products temperature has reached the eutectic point.
经验证明，过冷现象容易发生至使制品温度虽已达到共晶点。
With the increase of modifying temperature, the modification of rare earth Pr enhances on primary silicon, fades on eutectic silicon.
随着变质温度的升高，稀土对初晶硅的变质作用加强，而对共晶硅的变质作用减弱。
The influence of heating temperature on morphology of eutectic carbide and impact fatigue property of low alloy wear resistant cast iron were studied by OM, SEM and impact fatigue tester.
采用金相、扫描电镜和力学性能分析方法研究了加热温度对含稀土低合金耐磨铸铁冲击韧性的影响。
The cast eutectic volume fractions are remarkably reduced with increasing HIP temperature.
提高热等静压温度能显著减少共晶含量。
Comparing with fluoride eutectic fluxes, it possesses the advantages as: low melting temperature, good wetting ability, easy to prepare, etc.
与氟化物共晶型钎剂相比，有熔点低、流动性好、制备方便等优点。
The results show that the eutectic transformation temperature of gray iron decreases with the increase of antimony content.
结果表明，随着锑含量的增加，灰口铁共晶转变温度降低；
The effect of Nb on the as-cast microstructures and the prespheroidization at elevated temperature of eutectic carbides of M2 high speed steel was studied.
研究了铌对M2高速钢的共晶碳化物组织和共晶碳化物高温球化的影响。
On the non preheating cladding layer, the eutectic austenite dendrite growth is along the opposite direction of temperature gradient beginning from interface to face of cladding layer.
在未预热的熔覆层内，先共晶的奥氏体枝晶的生长，从界面开始逆温度梯度方向定向生长．直到熔覆层的表面。
As the superheat temperature being enhanced, the size of carbides eutectic cells increases and tensile properties decline at room temperature.
随着过热度的增加，碳化物共晶团的尺寸增大，导致室温拉伸性能降低。
As the superheat temperature being enhanced, the size of carbides eutectic cells increases and tensile properties decline at room temperature.
随着过热度的增加，碳化物共晶团的尺寸增大，导致室温拉伸性能降低。