The elongation increases obviously when the temperature is increased.
伸长率随温度升高而明显增加。
Breaking elongation increases with the increase in treatment temperature.
纱线断裂伸长随着处理温度的增加而增加。
The flow stress decreases and the elongation increases with the decrease of stress rate .
随着拉伸速度的减小，合金的流变应力减小，延伸率增大。
The results showed that the tensile strength and yield strength decrease while total elongation increases with decreasing quenching temperature.
结果表明，随着淬火温度的降低，双相钢的屈服和抗拉强度下降，同时总伸长率提高；
The drawing force decreases and the specific elongation increases when the frequency of pulse current exerting to wire adds in the scope of experiments.
在实验范围内，施加的脉冲电流频率增加时，拉拔力降低，合金丝的延伸率增加。
The microhardness and tensile strength of stir zone increase compared with the base material, and the elongation increases significantly due to its fine and uniform microstructure of the specimen.
搅拌区细晶组织的显微硬度及抗拉强度相比于铸态母材有所提高，而伸长率显著提高。
Under the high-temperature conditions, all the samples fracture in the side of aluminum; with the rise of temperature, tensile strength of the joint declines obviously, while elongation increases;
高温条件下，试样均断于铝端母材，抗拉强度随着温度的升高呈现出明显的下降趋势，而伸长率随温度升高而增大；
The results show that the properties, especially elongation of low pressure sample castings increases dramatically under the same conditions of melting and heat treatments.
结果表明，在相同的熔铸工艺和热处理条件下，调压铸造试样的强度，特别是伸长率得到大幅度提高。
Increase in the amount of MTES increases the tensile strength and decreases the ratio of elongation for breaking of the materials.
并且随着MTES量的增加，材料的拉伸强度增强而断裂伸长率逐渐降低。
The tensile strength of the ionomers increases and the ultimate elongation decreases with the increase of sulfonate content.
随着磺酸盐含量的增加，离聚体的拉伸强度增大，伸长率下降。
The results indicate that the ultimate tensile strength of AM60B increases prominently with the increasing of RE, the yield strength and elongation are also improved.
结果表明，AM60B的抗拉强度随着RE的增加有显著提高，屈服强度、伸长率也有所提高。
The results show that: with the initial principal stress direction angle increases, the axial residual deformation from the compression state gradually transits to the elongation.
结果表明：随着初始主应力方向角的增大，轴向残余变形由压缩状态的正值逐渐过渡到伸长状态的负值。
As a result, n-butylamine as chain-extension agent decreases the inter action of molecular and increases the elongation of PU to 1400%.
结果表明，以正丁胺为扩链剂，可以减小聚氨酯分子间的作用力，提高分子的柔顺性，其断裂伸长率可达1400％以上；
They are always symmetrical about the horizon and move in opposite directions through the houses as the elongation of the Moon from the Sun increases.
他们总是关于地平线对称，并在各宫作反方向移动，因为太阳从月亮的距离增加。
The tensile strength for LLDPE/EVA blends increases as ATH content is increased, but elongation at break decreases.
随着ATH含量的增加，LLDPE/EVA共混物的拉伸强度逐步增加，断裂伸长率迅速下降。
The main reason that rare earth cerium can improve elongation of ZA27 alloy is that cerium increases the compositional undercooling of the alloy.
稀土铈改善ZA2 7合金塑性的主要原因是铈增加了合金的成分过冷。
The web also increases the entanglement density in the amorphous region and thereby has the effect of increasing breaking elongation and impact strength.
这种网络增加了非晶区内的缠结点密度，使材料的断裂伸长率和冲击强度提高；
The test has shown that as the degree of profile increases, the initial modulus and the breaking strength and elongation of profile yarn decreases. We have also quined the findi...
试验表明，在相同纺丝条件下，涤纶三叶异丝的断裂强伸度和初始模量随丝条异形度的提高而降低，而断裂强伸度变异系数、沸水收缩率和条干不匀率却随之增大。
The test has shown that as the degree of profile increases, the initial modulus and the breaking strength and elongation of profile yarn decreases. We have also quined the findi...
试验表明，在相同纺丝条件下，涤纶三叶异丝的断裂强伸度和初始模量随丝条异形度的提高而降低，而断裂强伸度变异系数、沸水收缩率和条干不匀率却随之增大。