The crystal defects were studied by optical method and chemical etching method.
用光学法和化学腐蚀法研究了晶体的缺陷，并分析了缺陷成因。
Planar crystal defects in a synthesized diamond were studied by synchrotron radiation topography.
利用同步辐射对合成金刚石晶体中面状缺陷进行了形貌学研究。
Also there are a lot of crystal defects, such as dislocations and twins, found near the interface.
同时在界面附近存在着大量位错和孪晶等晶体缺陷。
The stacking fault and other crystal defects in the crystal structure of parisite have been discussed.
讨论了氟碳钙铈矿结构中的堆垛层错等晶体缺陷现象。
The enhancement of Nb-Si-N films' mechanical properties is relative to the increment of crystal defects.
薄膜力学性能的提高与其晶体缺陷的增加有关。
The density of crystal defects in the region near the crystal surface is greater than that in the center.
晶体的靠近表面的区域缺陷较密集，中心部分较少。
The shunt resistance represents the loss due to surface leakage along the edge of the cell or due to crystal defects.
分流电阻表示由于沿电池边缘的表面漏流或晶格缺陷造成的损耗。
The crystallinity of LDPE increased firstly and decreased later and the crystal defects might increase as drawing rate increased.
随牵伸速率的增大，LDPE相结晶度出现先增加后减小的变化，晶体缺陷增多。
Point defect is the most fundamental but the most important one of crystal defects, existing at a certain concentration in all materials.
点缺陷是最基本的也是最重要的一类晶格缺陷，材料中或多或少的都存在一定浓度的点缺陷。
For the whole process of annealing, the leading factor for the change of activity of the al alloy anode was the change of crystal defects.
整个退火过程中，晶体缺陷的变化对铝阳极活性改变影响最大。
Crystal etching, a traditional method to study the crystal symmetry and crystal defects, should be a new application in modern mineralogy.
矿物晶体腐蚀像是一种研究晶体对称、晶格缺陷等传统的方法。
It indicates that the shape of W and WC grains is varied, such as dendritic and chain structure, and there are many crystal defects in WC grains.
发现钨和碳化钨粉形状复杂，多为树枝状或链状颗粒团形式，碳化钨粉中有较多的晶体缺陷。
We measured the spread noise of doped LiNbO_3 crystals, finding out the relation between the crystal defects and picture quality according to the experiment.
测量了晶体样品的散射噪声，从中找出了晶体缺陷与存储图像质量关系。
For the whole process of homogenizing annealing, the leading factor for the change of Al-alloy-anode's activation properties is the change of crystal defects.
整个退火过程中，晶体缺陷的变化对铝合金阳极活性改变影响最大。
Usually, if explosive particles have less crystal defects, more smooth surface, and higher crystal density, the explosives have lower sensitivities and better safety.
通常讲，具有更少的晶体缺陷，更光滑的外形、更高的晶体密度，则有利于降低炸药的感度，提高安全性。
Basic models are treated across traditional disciplines, not only in the discussion of methods but also in chapters on crystal defects, microstructure, fluids, polymers and soft matter.
基本模型是跨越传统学科的治疗，不仅在方法上的讨论，而且在晶体缺陷，微观结构，流体，聚合物和软物质的章节。
The effect of Si on the crystal lattice parameters, lattice volume and crystal defects of the eutectic cementite in malleable cast iron has been studied by using X ray diffractometer and TEM.
采用X-射线衍射仪、透射电镜研究了可锻铸铁白口组织中硅对共晶渗碳体点阵参数、晶胞体积及晶体缺陷的影响。
Analyzing the formation of growth morphology, the research proves that the crystal defects affect crystal growth. It can be concluded that the 2d nucleation and crystal defects control calcite growth.
论文初步分析了晶体表面形貌形成的原因，证明晶体中的各种缺陷也影响了晶体生长，由此得出方解石晶体表面形貌的形成是二维成核生长机制与缺陷生长机制共同作用的结果。
These defects appear during crystal growth, but crystals having such defects are not considered usable for ic manufacture and are discarded .
这些缺陷在晶体生长时出现，有这类缺陷的晶体不能用于集成电路制造，应报废。
The surfaces or interfaces structure of KDP crystals acquires the key importance for the crystal growth and defects formation.
KDP晶体的表面及界面结构对于晶体的生长及缺陷的形成具有重要影响。
A homogeneous dislocation defect model was established to study the sonic waveguide of a photonic crystal with defects.
为了研究声子晶体因缺陷而产生的声波导问题，提出了同质位错缺陷模型。
The crystal structure and some defects such as tilt boundary and dislocation of lanthanum chromates were investigated by high resolution microscopy (HERM).
用高分辨电子显微镜对铬酸镧的晶体结构及晶界、位错等晶体缺陷进行了观察与分析。
Of the defects detection system of the shell of crystal oscillator, obtaining high quality preprocessed image is prerequisite to correctly verify the defects.
在晶振外壳缺陷检测系统中，正确识别缺陷的前提条件是得到高质量的预处理图像。
The growth defects of the new nonlinear CLBO crystal are investigated and results are also discussed.
本文对新型非线性晶体CLBO的生长缺陷进行了分析研究。
The results showed that the metallurgical defects such as inclusions, coarse crystal grains and asymmetry of the grain size were the main reason resulting in fracture of the steel rods during drawing.
结果表明，原材料中存在的夹杂物、晶粒粗大及混晶等冶金质量缺陷是盘条在拉拔过程中发生断裂的主要原因。
The disadvantage of sheet-light is divergent and can not make more small defects, and can only use thin crystal in experiment.
缺点是经圆柱透镜形成的片光具有发散性，不能制作小数量级的缺陷，并且实验中只能使用薄晶体。
The different recombination properties of defects may be explained by means of the distribution of impurities during crystal growth.
晶锭凝固过程中的杂质分布以及杂质和缺陷之间的作用，决定了不同凝固位置缺陷的复合特性。
Nitrogen has a heavy impact on the properties of the single crystal silicon, and its properties, forms and mechanisms on reactions with related defects have been intensively investigated.
氮杂质对硅单晶的性质有重要的影响，氮在硅中的性质、存在形态以及和相关缺陷作用机理一直为人们所研究。
At present, photonic crystal waveguides, which are fabricated by introducing linear defects in two dimensional photonic crystals, have become an important research direction in this field.
目前二维光子晶体中引入线缺陷形成的光子晶体波导是该领域内的一个重要研究方向。
At present, photonic crystal waveguides, which are fabricated by introducing linear defects in two dimensional photonic crystals, have become an important research direction in this field.
目前二维光子晶体中引入线缺陷形成的光子晶体波导是该领域内的一个重要研究方向。