The results show that the cracking of the tap valve is brittle crack, which is due to overheat to cause the formation of defects, such as coarse grains, Widmanstatten structure and porosity.
结果表明，水龙头阀体开裂是由于存在过热造成的晶粒粗大、魏氏组织、铸造疏松等缺陷引起的脆性开裂。
The results show that the cracking of the tap valve is brittle crack, which is due to overheat to cause the formation of defects, such as coarse grains, Widmanstatten structure and porosity.
结果表明，水龙头阀体开裂是由于存在过热造成的晶粒粗大、魏氏组织、铸造疏松等缺陷引起的脆性开裂。