The experimental results showed that in the annealing condition the recrystallization texture has an important influence on the capacitance of etched al foil.
实验表明：在退火条件下，再结晶织构对腐蚀铝箔的电容量有重要影响。
The emphasis is put on effect of purity homogenization, hot rolling temperature, cold rolling and medium annealing on cubic texture of finally annealed foil.
重点研究了铝的纯度、均匀化制度、热轧温度、冷轧及中间退火对最终退火后箔材形成立方织构的影响。
The effect of extrusion ratio, temperature and electric field annealing on microstructure and texture of AZ31 magnesium alloy were investigated.
研究了挤压比、挤压温度及电场退火对AZ31镁合金组织和织构的影响。
The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.
采用晶体取向分布函数（ODF）、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。
The results show that hot rolling and normalizing annealing processes have significant influence on the cold_rolled texture of silicon steel.
结果表明：热轧及常化退火工艺对硅钢冷轧织构有显著的影响。
The results show that the intermediate pre-annealing process can affect the selection of crystalline texture.
结果发现，中间温度预退火过程可以影响薄膜对晶型结构的选择。
The effect of middle annealing on cube texture of high-purity aluminum foils was investigated by means of orientation distribution functions (ODFs).
采用晶体取向分布函数（ODF）研究和分析了中间退火对高纯铝箔立方织构的影响。
The structure and texture of continuous or batch annealing deep drawing and extra-deep drawing steel sheets were observed and analyzed.
对连续退火或罩式退火后的深冲钢板和超深冲钢板的组织以及织构进行了观测和分析。
The effect of annealing temperature on fibrous texture of cold rolled IF steel sheet rolled from strip hot rolled in ferrite region was investigated.
研究了铁素体区热轧if钢经冷轧后，不同退火温度对丝织构的影响。
The occupancy of cube-texture increases fast with the increase of final annealing temperature.
随最终退火温度的升高，立方织构占有率快速增长。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。