过去那种认为高炉生铁含碳量已经达到饱和并与铁水渗碳过程无关的看法是不正确的。
It is wrong to think that the content of iron has already been saturated and is not telated to the process of carburization.
文章阐述了新钢公司铁合金厂生铁高炉强化冶炼过程中的做法，出现的问题和护炉保产措施。
Measurement of guarding the france and increasing the production in strengthening smelting process of pig iron BF at ferroalloys plant of Xinsteel are expounded.
这种球团矿用于高炉冶炼含锰量较高的生铁，可以改善高炉冶炼技术经济指标和提高锰的回收率。
With using these pellets in blast furnace for making pig iron with higher manganese content the BF operation data improved and the recovery of manganese increased.
生铁：从高炉直接炼得并在模中铸出的粗铁。
Pig iron: Crude iron obtained directly from the blast furnace and cast in molds.
为了获得低硅炼钢生铁，必须控制高炉内硅的还原过程。
In order to obtain low silicon iron for steelmaking the reduction process of silicon must be controlled in blast furnace.
烧结矿是高炉炼铁的主要原料之一，其强度的高低直接影响高炉顺行的程度，最终影响到生铁的产量和质量。
Sinter is the main material of iron making. Its strength straightly influences the natural production of blast furnace, and it affects the yield and quality of the pig iron.
利用引射器将低压焦炉煤气引入高炉热风炉中以提高风温，达到了降低焦比、提高生铁产量之目的。
Coke gas was introduced into blast furnace hot air stove by use of ejector to increase air temperature so as to achieve the aim of reducing coke rate and increasing the production.
与高炉炼铁相比，熔融还原有利于获得较低磷含量的生铁。
The pig iron with low content of the phosphorous can be obtained by the smelting reduction in comparison with the blast furnace.
提出以我国辽东地区硼铁矿经高炉分离后的含硼生铁为原料直接冶炼硼钢。
Boroncontaining pig iron got from ludwigite ore in the eastern area of Liaoning province by blast furnace separation was proposed as raw material to directly smelt boron steel.
实践表明，渣铁沟浇注料工艺的实施和不断完善，是高炉强化冶炼、降低生铁成本的重要技术措施。
Practice indicates that application of and improvement on the casting process is an important technical measure to ensure efficient smelting and low cost of pig iron.
与高炉炼铁相比，熔融还原有利于获得较低磷含量的生铁。
The pig iron with low content of the phosphorous can be obtained by the smelting reduction in comparison with the blast…
实践表明，6号高炉采取优化参数等措施后，生铁一级品率有了明显提高。
The practice shows that the rate increases obviously after improving measures such as optimizing parameters of No. 6 BF are made.
改善高炉终渣的粘度温度性能，提高渣、铁分离能力是防治产生铁沟沉积物的有效措施。
The effective preventing measures are improving the fluidity of final slag and separation of slag from hot metal.
改善高炉终渣的粘度温度性能，提高渣、铁分离能力是防治产生铁沟沉积物的有效措施。
The effective preventing measures are improving the fluidity of final slag and separation of slag from hot metal.