报道了一种以表面活性剂、丙二烯二胺和柠檬酸、EDTA为主要组分的硫化亚铁清洗剂配方和其在炼油装置应用的情况。
A detergent for cleaning iron monosulfide was formulated with surfactant, diamino-propadiene, citric and EDTA, and its cleaning mechanism was discussed.
水在硫化亚铁的自热和自燃过程中有至关重要的作用。
Water played an important role in self-ignition of ferrous sulfide.
简述了化工设备硫化亚铁垢的形成、存在形式及分布；
The form and distribution of ferrous sulfide in chemical equipments are briefly discussed.
油品储罐中硫化亚铁氧化放热是引起油品自燃的主要原因。
The exothermal reaction of the iron sulfide in oil storage tanks was the main cause of self-ignition of the oil products.
油田中的老化油是指积存时间长、硫化亚铁等大量滋生而难以处理的原油。
The aging crude oil of oil fields is the oil over a long time and has a large number of breeds such as FeS, which is difficult to deal with.
对表面活性剂和反硝化细菌协同处理含硫化亚铁颗粒污油的可行性进行了研究。
Feasibility of synergistic treatment of iron sulfide laden and stabilized slops simultaneously by use of surfactant and sulfide scavenger was studied.
研究了在微波作用下，以硫化亚铁为催化剂，将H2S分解为氢气和硫磺的反应。
The reaction process of decomposing H2S into hydrogen and sulfur through microwave action with the ferrous sulfide as catalyst is studied.
对表面活性剂和硫化物去除剂协同处理含硫化亚铁颗粒污油的可行性进行了研究。
Feasibility of synergistic treatment of iron sulfide laden and stabilized slops simultaneously by use of surfactant and sulfide scavenger was studied.
应用结果表明：选择化学清洗预防硫化亚铁自燃，效果明显，且无腐蚀、无污染，简单、快捷。
The result showed that by using chemical cleaning media to prevent autoignition of ferrous sulfide, the effect is obviously good with no corrosion, no pollution, and simple and quickly.
详述了GW- 101型硫化亚铁钝化剂的性质特点以及在扬子石化加氢裂化装置的应用情况。
The characteristic of type GW-101 ferrous sulfide passivant and its application instance in hydrogenation cracking plant in YPC were described in detail.
阐述了硫化亚铁自燃的机理，分析了硫化亚铁自燃的案例，提供了防止硫化亚铁自燃的措施和方法。
The principle of ferrous sulfide self-ignition was described. Two cases were analyzed and provide some recommendations to prevent it.
通过一起石脑油罐的爆炸事故，分析了含硫油品储罐硫化亚铁自燃机理，并提出了预防同类事故的防范措施。
Through an explosion accident of naphtha tank, the spontaneous burning mechanism of FeS in sulfur contained oil tank was analyzed, and the protection method was, then, presented.
本研究利用自制的纳米尺寸的硫化亚铁颗粒作为等离子喷涂的喂料，在钢基体表面制成了纳米硫化亚铁自润滑涂层。
In this paper, the nano iron sulfide plasma spraying feedstocks were made by oneself and the nano self-lubricating coatings on the steel were fabricated by plasma spraying.
利用原子力显微镜(afm)、扫描电镜(sem)和光学显微镜观察分析了硫化亚铁喷涂层的表面、截面与磨面形貌。
AFM, SEM equipped with EDX and optical microscope were employed to observe and analyze the morphologies of the surface, cross-section and wear scar of the coatings.
综述了多种硫化物自润滑涂层的制作工艺，着重介绍了最新开发的纳米硫化亚铁热喷涂涂层的工艺、形貌、性能以及应用前景。
The new invention on nano-structured sulfide self-lubricating coatings produced by thermal spraying was specially introduced by showing their technology, appearance and capability.
综述了多种硫化物自润滑涂层的制作工艺，着重介绍了最新开发的纳米硫化亚铁热喷涂涂层的工艺、形貌、性能以及应用前景。
The new invention on nano-structured sulfide self-lubricating coatings produced by thermal spraying was specially introduced by showing their technology, appearance and capability.