讨论了煅烧温度对材料循环性能的影响。
The effect of sintering temperature on the cyclic performance for materials was discussed.
分析了添加籽晶和煅烧温度对粉体性能的影响。
The effects of seeds and the calcination temperature on the properties of the powder were studied.
钛柱撑膨润土的制备过程中，煅烧温度至关重要。
During the synthesis process of titanium oxide pillared bentonite, the calcinations temperature is the most important.
选取的参数为：煅烧温度和保温时间(煅烧时间)。
The calcine temperature and lasting time were selected as technological parameter during the calcining process.
结果表明煅烧温度是干法制备氧化铁颜料的一个重要因素。
The results showed that calcinate temperature was an important factor in the preparation process of iron oxide.
用TG - DTA法确定前驱体热分解过程及煅烧温度。
The thermal decompose progress and calcined temperature of precursor was determined by TG-DTA.
研究结果表明：适宜的煅烧温度有利于内蒙古煤矸石活化。
The results showed that:appropriate calcining temperature and holding time were conducive to the activation of coal gangue.
本文探讨了这类渣的矿物组成、煅烧温度与胶凝性能的关系。
This paper presents investigation on the relationship between cementitious properties and mineral components and burnt temperatures of such slags .
激活剂用量和煅烧温度影响荧光粉的发光亮度，是主要控制因素。
The flux dosage and calcination temperature, which affect luminosity of the fluorescent powder, are the major controlling factors.
研究了燃料种类及煅烧温度对合成产物相组成和粉末形貌的影响。
The influences of fuels and various calcinations temperatures on the phase components and microstructure of combustion synthesized products are described.
测试了样品的性能，讨论了煅烧温度、吸附时间对吸附性能的影响。
The property of the granular bentonite was measured, the influences of calcinations temperature and absorbed time on adsorption property were discussed.
研究认为 ，提高煅烧温度并快速冷却是提高熟料质量的重要途径。
The study shows that increased burning temperature with quick quenching is and important way to increase the clinker quality.
测试了样品的性能，讨论了煅烧温度、吸附时间对吸附性能的影响。
The calcinations temperature and ageing time influence the performance of desulphurization gypsum.
测试了样品的性能，讨论了煅烧温度、吸附时间对其吸附性能的影响。
The property of the sample was measured, and the effect of calcination temperature, absorbing time on adsorption reaction was discussed.
研究表明：氧化镁的活性和煅烧温度、时间及氧化镁中的硼含量有关。
It shows that the calcined temperature, calcined time and boron content relate with the activity of magnesium oxide.
在此方法中，煅烧时间、煅烧温度、葡萄糖含量对产物性能影响很大。
In the method, glucose content, calcination temperature, and calcination time have important effects on the performance of LiFePO4.
结果表明，球磨处理和粉体煅烧温度对HA坯体的烧结行为均有明显影响。
The results showed that ball-milling treatment and calcining temperature exert an influence on sintering process of HA.
分别考察了煅烧温度、反应温度对催化剂活性及生成碳纳米管形态的影响。
The effects of calcination and reaction temperatures on the reactivity of the catalyst and the morphology of carbon nanotubes were studied.
研究结果表明：(1)煅烧温度是影响加气混凝土脱水相活性的主要因素。
The main results are as follows: (1) Heat treatment temperature is the main factor that impacting the reactivity of dehydrated aerated concrete (DAC).
在不同的煅烧温度、颗粒粒径和二氧化碳浓度下对石灰石颗粒进行热重分析。
The calcinations reaction of limestone particle was studied by thermogravimetric analysis. The effects of calcinations temperature, particle size and CO2concentration were investigated.
研究结果表明，阳极基体煅烧温度对LSGMC膜的电学性能具有强烈的影响。
The results show that the calcining temperature of the anode substrate strongly affects the electrical properties of LSGMC films.
研究了石灰石粒度、煅烧温度和时间对小颗粒石灰石煅烧制备高活性度石灰的影响。
The influences of particle size, calcining temperature, and time on the preparation of lime with high activity from small particles of limestone were studied.
以稀土为激活剂的长余辉磷光体，它的余辉亮度主要受原材料配比和煅烧温度的影响。
The brightness of long decay phosphors composed of rare-earth activator depends on the components of the raw material and temperature of fire.
研究结果表明，铟锡氧化物的相组成在很大程度上依赖于前驱体的相组成和煅烧温度。
It was found that the phase composition was mainly depended on their precursors' phase and annealing temperature.
详细讨论了煅烧制度，如煅烧温度、升温速率和却冷方式对最终产物晶体结构的影响。
The effects of calcination system and cooling mode on crystal structure of the products were discussed.
研究了白云石的煅烧温度、保温时间以及掺量等对水泥物理性能和膨胀行为的影响规律。
In this paper, the effects of calcination temperature, holding time and content of dolomite on the strength and expansion rate of cement mixed with calcined dolomite are investigated.
对不同温度下煅烧煤矸石水泥混合材进行了系统研究，以寻找煤矸石活性的最佳煅烧温度。
The systematic research was carried out for coal gangue calcined at different temperatures, which was used as cement mixture, so as to find the optimum temperature for activation of coal gangue.
研究了不同的煅烧温度及保温时间对脱硫石膏-粉煤灰新型复合胶凝体系抗压强度的影响。
The effect of different calcination temperature and the maintaining time at a certain temperature on the compressive strength of flue gas desulphurization gypsum-fly ash composite were studied.
实验结果表明：煅烧产物由煅烧前的晶态转变成了非晶态，煅烧温度对煅烧产物的结构有一定影响。
The results show that the calcined kaolin has been transformed from crystallized kaolin to non-crystal one, and calcinate temperature has some influence on its structure.
实验结果表明：煅烧产物由煅烧前的晶态转变成了非晶态，煅烧温度对煅烧产物的结构有一定影响。
The results show that the calcined kaolin has been transformed from crystallized kaolin to non-crystal one, and calcinate temperature has some influence on its structure.