Fretting wear behavior of K417 nickel base superalloy was investigated.
研究了K417镍基高温合金的微动磨损行为。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
通过自制的冲击腐蚀磨损试验机，施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
The results show that the alloy possesses fine and uniform microstructure and excellent wear resistance in which slide and abrasive wear are dominant in the wear behavior.
研究结果表明：半固态挤压成形合金具有细小、均匀的微观组织和良好的耐磨性，磨损失效形式以滑动和磨粒磨损为主。
The impact wear behavior of AZ91D magnesium alloys in de-ionized water has been investigated. The results showed that the depth and area of wear scar increased with the impact cycles.
研究了AZ91D镁合金在冲击载荷和去离子水介质综合作用下的磨损特性。结果表明，镁合金表面冲击斑深度及面积随冲击次数的增加而增加；
Friction force measurements during unlubricated pin-on-disc sliding tests, profilometry and SEM analysis of wear tracks are used to determine the wear behavior quantitatively and qualitatively.
摩擦学性能由销一盘式试验过程中的摩擦力数据和对磨痕的表面轮廓仪和扫描电镜分析作出定量、定性的评价。
In the high wearing area of the big particle, wear behavior includes many kinds of mechanism, and the superficial microstructure is also very complicated.
在大颗粒的高磨损区，磨损行为包含多种机理，表面的磨损形貌也很复杂。
In the high wearing area of the big particle, wear behavior includes many kinds of mechanism, and the superficial microstructure is also very complicated.
在大颗粒的高磨损区，磨损行为包含多种机理，表面的磨损形貌也很复杂。