It was found by SEM that the interaction between Mg (OH) 2 and EPDM was improved by adding MAA.
扫描电镜分析表明，MAA的加入增强了氢氧化镁与EPDM之间的相互作用。
At last, we tested the processing and mechanical properties of AN/MAA copolymer foam sandwich core material.
探索了AN/MAA共聚物泡沫塑料夹层结构复合材料的成型加工性和力学性能。
This paper introduces briefly the contributions that Professor Maa Dahyou has made in architectural acoustics.
本文仅就马大猷教授在建筑声学领域内做出的贡献，作简要的介绍。
Vinyl sulfonate monomers were experimentally found of lower reactivity and couldn't effectively copolymerize with MMA and MAA.
实验发现乙烯基磺酸酯类单体活性较低，与MMA和MAA单体聚合时不能很好的参与聚合反应。
The Mathematical Association of America (MAA) will designate one Outstanding Team from each problem for the MCM as a MAA winner.
美国数学协会（MAA）将从MCM的每个题目中指定一个杰出队作为一个MAA赢家。
The results suggest that after goats' fast infusing into duodenal with MAA and MVFA can significantly inhibit the release of motilin.
说明山羊禁食后十二指肠灌注混合氨基酸和混合挥发性脂肪酸能显著抑制胃动素的释放。
The polymer was prepared by copolymerizing vinyl sulfonate, methyl methacrylate(MMA) and methacrylic acid(MAA) in different proportions.
三元树脂由乙烯基磺酸酯、甲基丙烯酸甲酯（MMA）与甲基丙烯酸（MAA）按不同的配比共聚而成。
The cycle-reaction of the MAN-MAA-MAM copolymers at high temperature and the thermal-properties of polymethacrylimide(PMI) were investigated.
详细研究了所制备共聚物的高温环化反应，以及所生成的聚甲基丙烯酰亚胺（PMI）的耐热性能。
Using emulsion polymerization, a conductive polymer composite was synthesized with polyaniline as shell , the polymer acid obtained by MMA MAA and BA as core.
采用核壳乳液聚合方法合成了以甲基丙烯酸甲酯、 甲基丙烯酸和丙烯酸丁酯三元共聚物酸为核，聚苯胺为壳的导电高分子复合物。
Silane-graft-epoxy water dispersion was synthesized by copolymerization of epoxy resin, vinyltriethoxysilane (VTES), methylacrylic acid (MAA), and styrene (St).
本文以反应性乙烯基三乙氧基硅烷（VTES）为接枝单体，合成了一种新型有机硅烷接枝环氧树脂水分散体。
The OMP designation will result in reduced Marketing Authorization Application (MAA) fees, free access to scientific advice from the EMEA and other potential research and development incentives.
OMP指定将导致降低的销售授权应用（MAA）费， 使科学建议的入口与EMEA和其他潜在的研究与开发奖励分离。
The in-situ preparation of zinc methylacrylate or zinc acrylate through mixing zinc oxide(ZnO) and methylacrylic acid (MAA)or acrylic acid(AA) in NBR rubber vulcanized with peroxide was studied.
通过氧化锌与甲基丙烯酸或丙烯酸的中和反应，在丁腈橡胶（NBR）中原位生成了甲基丙烯酸锌或丙烯酸锌，研究了过氧化物硫化NBR的力学性能和交联结构。
The in-situ preparation of zinc methylacrylate or zinc acrylate through mixing zinc oxide(ZnO) and methylacrylic acid (MAA)or acrylic acid(AA) in NBR rubber vulcanized with peroxide was studied.
通过氧化锌与甲基丙烯酸或丙烯酸的中和反应，在丁腈橡胶（NBR）中原位生成了甲基丙烯酸锌或丙烯酸锌，研究了过氧化物硫化NBR的力学性能和交联结构。