Hot cracks commonly occurred in inside weld as the forming process of SSAW pipe.
螺旋埋弧焊管在成型过程中容易产生内焊热裂纹。
Inside weld produced cracks are often faced problem by adopting wide coil with small forming Angle to produce small size spiral submerged welded pipe.
采用宽板小成型角生产小口径螺旋缝埋弧焊钢管时，内焊缝产生裂纹是经常遇到的问题。
Through analysis on inside weld forming and welding procedure of SSAW pipe, it pointed out weld crack is easy to appear in brittle temperature zone in welding pool.
通过对螺旋埋弧焊管内焊缝成型和焊接过程的分析，指出焊缝裂纹易产生在焊接熔池脆性温度区。
The longitudinal cracks along bond line and the transverse cracks which cut across the weld metal cross section inside weld metal were formed, while X65 pipe line steel was welding.
X65管线钢在焊接过程中，内侧焊缝金属出现横向和纵向沿熔合线方向的裂纹，横向裂纹贯穿焊缝金属横截面。
On overall inspection of interior and exterior of pre-hydrogenating reactor of Shanghai Oil Refinery Factory, large cracks was found on the surface of weld and inside of the weld.
在上海炼油厂预加氢反应器投用前的内外部检验中，发现了大量的焊缝表面裂纹和内部埋藏裂纹。
Spot-weld the side wind ow aperture to the inside of the side section.
将侧窗接缝点焊到侧面部件内侧。
If the sheet is relatively thin, the range of welding parameters obtained that can get better weld quality is wider. Heavily plastic flow of the weld metal occurs inside the weld during the process.
板材厚度较小时，形成良好焊缝的规范参数范围较宽，焊接过程中接头内部发生了剧烈的塑性流动。
Fatigue beaked on weld seam more than other places. Fatigue crack initiation occurred inside materials and fatigue fracture was analyzed by SEM.
疲劳试验发现，疲劳试样断裂位置多发生在焊缝处，并对疲劳断口进行了SEM分析。
Fatigue beaked on weld seam more than other places. Fatigue crack initiation occurred inside materials and fatigue fracture was analyzed by SEM.
疲劳试验发现，疲劳试样断裂位置多发生在焊缝处，并对疲劳断口进行了SEM分析。