It was investigated that chromizing in borax salt bath and melting hydrochloride.
研究了硼砂盐浴渗铬和氯系熔盐渗铬。
Plasma chromizing was achieved on Q235 steel and 45 steel surface and formed high chrome layer.
采用双层辉光等离子渗金属技术先在Q235钢和45钢表面渗入元素铬，形成高铬合金层；
Under controlling technique factors, we have produced high quality chromizing cast-infiltration layer.
通过控制工艺因素，在铸铁件表面获得了质量完好的铸渗层。
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了T10钢在低温盐浴渗铬后直接淬火并回火工艺。
The wear resistance of hard alloy (YG14) and boronizing layer, boron-chromizing layer for steel 45 was studied.
研究了硬质合金(YG14)和45钢渗硼层、硼铬共渗层的耐磨性。
It is shown that a excellent chromized zone morphology is obtained and the chromizing rate is raised through...
结果表明辉光离子渗铬可获得良好的渗层组织并明显加速渗铬过程。
The results show that the addition of rare earth elements can increase the depth of the chromizing layer and hardnesss of the T10 steel surface.
结果表明，稀土能增加渗铬层深度，有助于提高渗氮层的表面硬度。
By observing and analyzing the casting test piece, we have found a metallurgical integrating layer that is made up of chromizing cast-iron alloy layer.
我们还对铸渗质量较好的铸渗试件进行了观察和分析，发现铸铁渗铬合金层与母材结合良好，呈冶金结合。
The results show that a compound layer with good wear-resistance and corrosion resistance can be gained in 304 austenitic steel by chromizing sbusequent solid soluti…
结果表明，304奥氏体不锈钢经渗铬固溶渗氮复合处理后可获得性能优良的复合渗层，且耐磨、耐腐蚀。
The results show that a compound layer with good wear-resistance and corrosion resistance can be gained in 304 austenitic steel by chromizing sbusequent solid soluti…
结果表明，304奥氏体不锈钢经渗铬固溶渗氮复合处理后可获得性能优良的复合渗层，且耐磨、耐腐蚀。