研究了K417镍基高温合金的微动磨损行为。
Fretting wear behavior of K417 nickel base superalloy was investigated.
讨论了施镀温度对镀层成分、结构和抗腐蚀磨损行为的影响。
The dependence of plating composition, structure and the behaviour of corrosive wear resistance on plating temperature is also discussed.
对一种硼酸铝晶须增强LY 12铝进行了干磨损行为研究。
This paper proceeds to investigate the dry wearing behavior of the aluminium borate crystal whiskered reinforced LY12 aluminium.
并与纯铜进行比较，探讨颗粒增强物对材料磨损行为影响的机理。
It was compared with the pure copper specimens to investigate the wear mechanism.
研究了不同的热处理制度下该钢的显微组织、力学性能及磨损行为。
The microstructure, mechanical properties and tribological behaviors of the steel treated by different heat treatments were studied.
研究了中碳含硅贝氏体钢不同组织结构对高应力冲击磨损行为的影响。
The high stress impact wear behaviors of bainite steel containing silicon with different microstructure were studied.
对所研制的高碳低合金耐磨钢的强韧化、耐磨性及磨损行为进行了研究。
Experiments were carried out upon the hardening and toughening, wear resistance and abrasive behaviour of the low alloyed high carbon wear resistant cast steel.
采用TE66试验机对新型TAMZ钛合金的微磨粒磨损行为进行了研究。
The micro-scale abrasive wear behaviors of TAMZ alloy were studied using a TE66 micro-scale abrasion tester.
在大颗粒的高磨损区，磨损行为包含多种机理，表面的磨损形貌也很复杂。
In the high wearing area of the big particle, wear behavior includes many kinds of mechanism, and the superficial microstructure is also very complicated.
因此，在高温高压水介质中的金属磨损行为是这两种不同影响因素共同作用的结果。
Thus, the wear behaviour of metals in high temperature and high pressure water is the combining results of these two different effects.
高温冲蚀磨损试验表明，各涂层的冲蚀磨损行为介于塑性与脆性冲蚀之间，并以塑性磨损为主。
The erosion tests at elevated temperature show that coating's erosion behavior is between plasticity and fragility.
通过自制的冲击腐蚀磨损试验机，施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
气泡和颗粒在流化床水平理管周围的运动行为与埋管传热和埋管磨损关系十分密切。
Movement of bubbles and particles around tube immersed in a fluidized bed is closely re lated to tube heat transfer and tube abrasion.
但是，我们发现，没有证据显示，这种现象在球磨机，而不是观察到的行为，是由于高应力磨损，在服务环境。
However, we have found no evidence of such a phenomenon in ball mills, and instead the observed behaviour is attributed to high stress abrasion in the service environment.
本文总结了金属、陶瓷、高分子及复合材料的磨损失效机制，以及不同材料磨损失效行为的主要区别。
The characteristic mechanisms on wear failure of metals, ceramics, polymers and composites were summarized, and wear failure behaviors of different materials were distinguished as well.
对经不同温度下热处理的镀层进行了显微硬度和XRD分析和腐蚀磨损电化学行为研究。
The HV and XRD results show that the hardening of deposition was due to crystallization during heat-treatment at different temperatures.
对经不同温度下热处理的镀层进行了显微硬度和XRD分析和腐蚀磨损电化学行为研究。
The HV and XRD results show that the hardening of deposition was due to crystallization during heat-treatment at different temperatures.