研究发现，在应力退火下两种合金都获得了横向感生磁各向异性；
The study shows that the alloys under stress annealing can obtain transversal induced magnetic anisotropy.
利用短时矩形脉冲电流对近零磁致伸缩系数钴基非晶态合金带进行退火处理，得到约114%的巨磁阻抗变化率。
The GMI ratio of about 114 % is obtained in near zero-magnetostrictive Co-based amorphous alloy ribbon annealed by short time rectangular pulse current.
本发明还提供了上述 铁氧体磁粉的制备方法，其包括以下步骤：配料、混料、预烧、粗破碎、细磨、烘干、退火、解碎。
The invention also provides the preparation method of the ferromagnetic oxide powder, comprising the steps of dosing, mixing, preburning, crude crushing, fine grinding, drying, annealing and smashing.
磁黄铁矿固治体从硫化物熔体结晶后，在缓慢冷却过程中经历了显著的退火。
Pyrrhotite solid solution, subsequent to crystallization from sulfide melt, will suffer strong annealing during slow cooling.
通过金相法和磁声发射法（MAE）研究了高牌号无取向硅钢脱碳退火时所产生的内氧化层。
The subsurface oxide layers generated during decarburizing annealing of high grade non-oriented silicon steel sheet were studied by metallographical method and magnetoacoustic emission method(MAE).
结果表明，磁场退火热处理可形成感生磁各向异性，改善薄膜的软磁性能、提高薄膜的应力阻抗效应。
The results show that magneto-annealing can improve film stress impedance effect and film soft magnetic performances, and induce magneto-anisotropy.
一定条件下进行电流退火能使样品的磁结构产生圆周各向异性，从而提高样品的巨磁阻抗效应。
In certain condition, DC Joule annealing can induce circular anisotropy among the ferro-magnetic layer of the samples, thus increases the ratio of the GMI effect of the samples.
首次从无规双相各向异性模型和快速循环退火法两方面入手，建立了RRTA纳米晶化动力学模型，给出了软磁薄膜的磁电性能与纳米晶化工艺的关系。
The crystallization kinetics model is established by using a random two-phase anisotropy film. The influences of RRTA parameters on magnetic and electric properties of soft-magnetic are studied.
磁芯经过二次退火后，由于封装胶发生膨胀使得被封装的磁芯电感值严重下降，软磁性能下降。
After cores being secondary annealed, expansion of packaging glue happen, which causes that the inductance value of magnetic-cores declined seriously, soft magnetic properties reduced.
磁芯经过二次退火后，由于封装胶发生膨胀使得被封装的磁芯电感值严重下降，软磁性能下降。
After cores being secondary annealed, expansion of packaging glue happen, which causes that the inductance value of magnetic-cores declined seriously, soft magnetic properties reduced.