在挤压过程中，发泡剂，注入在高压力。
In the extruding process, vesicant is injected at high pressure.
分析了液态挤压过程中金属的流动和变形特征。
Flow and deformation feature of the metal in the process of liquid extrusion were analysed.
对铜母线连续挤压过程的几何模型进行简化，基于MSC。
By simplifying the geometry model of the copper bus bar continuous extrusion process, based on a new metal forming simulation package, MSC.
实验研究了液态浸渗后直接挤压过程模具与坯料内部的温度变化。
The temperatures at different positions inside the die and the extruded-billet during extrusion directly following liquid infiltration were experimentally investigated.
各散热部在连接机构的挤压过程中在翘起部的作用下呈放射状展开。
The radiating parts are expanded radially under the action of the tilting parts in the squeezing process of the connecting mechanism.
运用有限元模拟的方法研究了内角半径在等径角挤压过程中的作用。
The effect of inner corner radius on the plastic deformation behavior in equal channel angular pressing was investigated using finite element method.
这个过程是主动运动，而不是由血液的流体静力压所致的被动挤压过程。
The process is one of active motility rather than passive extrusion by the hydrostatic pressure of the blood.
利用上限元法(UBET)模拟了圆柱直齿轮径向挤压过程的变形力规律。
Laws of the deformation force during radial extrusion of spur gear are simulated by using UBET.
铝合金反向挤压过程中，不同的挤压工艺条件对粗晶组织将产生不同的影响。
Among aluminium alloy indirect extrusion producing period, various process condition influence different result to the coarse grain structure.
这台机器采用了特殊设计的螺杆和桶，模具和挤压过程，以生产塑料和木材产品。
This machine USES the special designed screw and barrel, die and extrusion process to produce plastic and wood products.
对挤压过程热传递过程分析表明坯料冷却程度与其所处应力状态和保温介质有关。
It shows that the thickness of cooling hard layer is associated with the state of stress and heat preservation material by analyzing the heat transfer principle.
通过对挤压过程压制力和位移曲线的分析，提出了对挤压过程三个阶段的合理划分。
The extrusion is successfully divided into three ideal stages through the analysis on the pressing force and displacement curve in the process of extrusion.
通过对C12200铸锭的切片分析，提出挤压过程含磷类管材表面起泡的新见解。
By the analysis of cut piece of billet C12200, a new view is put forward for tube surface bubble of phosphorous copper in the extrusion.
运用变形功原理，推导出求金属塑性挤压过程中挤压力的一种极其简捷的近似计算式。
On the principle of the deformation work this paper words out a very simple method for approximate calculation of the extrusion force in the metalic plastic extrusion processes.
对机加生产的锥形体改为温挤压进行了研究，解决了挤压过程中出现的金属夹层问题。
Applying warm extrusion technique instead of machine 'work to a conical body, the problem of double-layered metal formed in the process of extrusion has been solved.
因此，在热挤压过程中，如何减少磨损、避免局部磨损过大是设计人员最关心的问题之一。
So, in hot extrusion process, how to reduce wear and improve die life is one of the most concerned problems for mold designer.
分析了6063铝合金型材在挤压过程中产生“停止痕”缺陷的原因，提出了相应的对策。
The causes for stop mark defect of extruded6063aluminium alloy profiles were analyzed. Some countermeasures were given.
记录了冷挤压过程中与不同变形程度相对应的挤压力，绘制了冷挤压过程的连续挤压力曲线；
And the extrusion force to different transfiguration degree was recorded to draw the continuous extrusion force curve during the cold-extrusion course.
用实验方法研究了中碳钢两相组织在等通道角挤压过程中的强烈塑性变形行为和组织演化过程。
Severe plastic deforming behavior and microstructure evolution of two phases in medium-carbon steel during equal channel angular pressing (ECAP) were investigated by experimental method.
简要介绍了挤压膨化法生产大豆组织蛋白的原理及影响因素，并介绍了挤压过程中物料的变化。
The principle, influence factor and material changes of preparing extruded soybean protein with twinscrewderevaporater are introduced.
针对粉末多孔材料，采用体积可压缩刚粘塑性热力耦合有限元法对其等径角挤压过程进行模拟分析。
The densification and deformation behavior of porous materials during the ECAP process were investigated by (thermo -) mechanical coupling finite element method.
通过网格实验研究了等截面侧向挤压过程中材料的变形情况，结果表明塑性变形区仅位于模具通道拐点连线附近。
The deformation pattern of ECSLE was investigated with grid experiment. The experiment result shows that the plastic deformation zone is a linear area between the two corners of die channel.
结果表明冷挤压过程中模具表面并非越光越有利于成形，坯料也要针对不同的挤压材料应选用不同的热处理方法。
The results show that according to different material, relevant heat treatment method and mold roughness, etc. must be chosen correctly.
该文详细论述早餐谷物原料中主要成分，如蛋白质、淀粉、脂类物质、膳食纤维及其它成分在挤压过程中所发生变化。
In this article, the changes in ingredients of breakfast cereals are discussed detail, such as protein, starch, lipids and diet fiber and so on.
研究了挤压过程中，挤压温度、螺杆转速、进料速度、原料水分含量对淀粉的糊化、降解及对挤出物的溶解指数和膨化度的影响。
This paper studies the influence of extrusion temperature. Screw speed, feed speed and water content on starch gelatinization depolymerization, soluble index and expansion efficiency.
在常规的铝及铝合金热挤压过程中，金属的温度和变形是很不均匀的，这将导致产品的尺寸、形状、组织和性能等质量方面的缺陷。
During conventional hot extrusion processes, temperature and distortion of the billets change unevenly, so the dimension, shape, organization and capability of the profile will be deterioration.
从熔铸工艺、挤压工艺、模具、挤压设备等方面分析了6063铝合金型材在挤压过程中产生表面条纹的原因，并提出了相应的对策。
The factors including of melting-casting process, extrusion process, die, and extrusion device resulting in the surface streaks of 6063 aluminium alloy profiles were analyzed.
从熔铸工艺、挤压工艺、模具、挤压设备等方面分析了6063铝合金型材在挤压过程中产生表面条纹的原因，并提出了相应的对策。
The factors including of melting-casting process, extrusion process, die, and extrusion device resulting in the surface streaks of 6063 aluminium alloy profiles were analyzed.
应用推荐