白口和反白口缺陷是球铁件转向节的常见缺陷。
Both the chill and reverse chill are defects often found in the nodular iron knucle castings.
这样就会认可反白显示的符号，就像完成模式一样。
The highlighted symbol is committed, just as it is in completion mode.
在此例中，大括号会保持反白显示直到移动游标为止。
In this case, the braces will remain highlighted until the cursor is moved.
下半部则会针对反白显示的资料表显示资料行详细资料。
The lower area displays column details for a highlighted table.
取得或设定值，指出是否在萤幕上反白显示共用活页簿的变更。
Gets or sets a value that indicates whether changes to the Shared workbook are highlighted on screen.
对于大断面球墨铸铁件，有防止球化不良和消除反白口的作用。
It has the effect keeping heavy section ductile iron casting from...
剪贴簿的内容会出现在新位置，而且仍保持反白显示，直到您按一下别处。
The Clipboard contents appear at the new location and remain highlighted until you click elsewhere.
由于反白显示是以背景工作执行，因此在标记反白显示之前可能会有些延迟。
Because tag highlighting is performed as a background task, there might be a small delay before the tags are highlighted.
介绍了球墨铸铁反白口缺陷的显微特征，对反白口的形成原因，防止措施进行了分析和讨论。
The characteristics of microstructure of the inverse chill in ductile iron are presented. The cause of the formation of inverse chill and its prevention are discussed.
接著会反白显示适当的符号，而非使用焦点矩形，而且您可以按向上键或向下键反白显示符号。
The appropriate symbol is then highlighted instead of having a focus rectangle, and you can press UP ARROW or DOWN ARROW to highlight symbols.
如果在绘制时进行反白，成为白底黑字，则会导致背景渗入前景，而且会使得某些用户难以阅读。
Drawing these reversed, as black text on a white background causes the background to bleed over the foreground and can make reading difficult for some users.
输入右括号后，右括号和其对称的左括号都会保持反白显示数秒钟，或是直到您按下其他按键或移动游标为止。
When you type a closing bracket, both it and its matching bracket remain highlighted for a few seconds, or until you type another key or move the cursor.
引起反白口的主要原因是残余镁量，特别是残余稀土量过高，防止措施是采用稀土含量较低的球化剂，提高球化处理温度和浇注温度。
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect. So them…
引起反白口的主要原因是残余镁量，特别是残余稀土量过高，防止措施是采用稀土含量较低的球化剂，提高球化处理温度和浇注温度。
Too high residual magnesium content, and especially too high residual rare earth content is the main reason causing reverse chill defect. So them…