Introducing the performance of spraying welding layer for nickel wearing resistance alloy.
介绍了镍基耐磨合金喷焊层的性能。
Used for welding of different iron welding layer can satisfy the requirements of color matching, tensile strength and ductility.
用于不同铸铁焊接时焊层能最大要求的满足其颜色匹配,抗拉强度和延展性优良。
The results showed that the forming of crack was mostly made by the interface defect between overlaying welding layer and matrix.
结果表明,堆焊层与基体的界面缺陷是裂纹形成的主要原因。
With SMAW method, the surfaces of A3 and 45 steel were welded by using the series of CHR electrode, and the microstructure and performance of surfacing welding layer metal were analyzed.
借助手工电弧焊方法,使用CHR系列堆焊焊条对A 3、45钢进行堆焊加工,分析了其堆焊层金属的显微组织及性能。
Detailed analysis is made of the reasons why fissures, peeling-off, and tooth breaking exist in the build-up welding layer of cast WC for hardening material of steel-toothed gear drills.
在钢齿牙轮钻头强化材料中,详细地分析了铸造碳化钨堆焊层产生龟裂、脱落和断齿的原因。
Layer can be used to connect steel stamping forming diamond-shaped network, with gas shielded welding spot on the plate.
连接层可用冲压成型的钢质菱形网,用气体保护焊接方法点焊于钢板上。
Attention to the need to shape the shape of plastic, steel welding, after a layer of steel wire mesh, and then began to shape the basic layer of paint.
注意需要塑出大概的形状,钢筋焊好之后,在外面扎一层钢丝网,然后开始塑造基础层粉刷。
Note about the shape of the need to model to the, steel welding, outside a layer of steel wire net, and then began to shape the base layer to paint.
注意需要塑出大概的形状臧,钢筋焊好之后,在外面扎一层钢丝网,然后开始塑造基础层粉刷。
The waterproof layer of the lap joint should stick (welding) firm, tight sealing, no distortion, fold, curling and blister defects.
卷材屋顶防水层的搭接缝应粘(焊)结牢固,密封精密,不得有扭曲、皱折、翘边和起泡等缺陷。
Throughcalculation of temperature rising callused by them, melt criterion is given, the thickness of melted layer near explosive welding interface with small collision Angle is estimated.
通过计算绝热压缩温升和畸变形能沉积产生的温升,给出熔化判据,定量估计出了在小碰撞角下爆炸焊接界面熔化层厚度。
By two double-mediate layer method, using developed welding materials and technology of forced arc molding, butt joining tests of high manganese steel with rail steel are completed.
采用两种过渡层方法,使用研制的过渡层焊接材料,结合强制成形电弧焊工艺进行了高锰钢辙叉与钢轨双过渡层对接焊试验。
Modern analytical methods have been used to investigate the patterns of fusion zone and the diffusion behaviors of elements by tig direct welding and tig with Sn as transition layer welding.
利用现代分析测试手段分别研究了TIG焊直接焊接镁铝和镀锡焊接镁铝的焊缝熔合区形貌,并对其进行了元素扩散行为的分析及比较。
Welding material selection of transition layer refers to the following table.
过渡层焊接材料的挑选参睹上里。
Welding smoke and dust dispersing in workshop influence peoples health directly; adopting divided layer blowing can improve effectively.
焊接烟尘弥散悬浮在车间,直接影响人体健康,采用分层送风方式可有效改善这一点。
This backing is used for one-side automatic welding to reinforce F/G layer. It is also easily used at bending parts.
本衬垫供单面自动焊接用F/G层的加强,也易用于弯曲部分。
This process totally avoids oxide layer on the welding material with the protection of argon, so guarantees the performance of the parts is the same with the metal of industrial titanium.
上述生产工艺由于彻底去除了氧化层并在焊接过程中采用了氩气保护,所以保证了加工成型后的钛配件与工业纯钛的性能一样。
The wear resistance of surfacing layer was investigated by the design of flux-cored wires and tig welding method.
通过药芯焊丝配方的设计,结合TIG焊接方法,对堆焊层的耐磨性进行了研究。
The invention has the advantages that: said medium layer can improve the welding property and avoid the effect of dissociate graphite.
本发明的积极效果是:通过这层介质解决了铸件的可焊性,并阻隔了游离状态石墨的影响。
Metal waterproof layer connectivity to the welding, and anti-corrosion protection brushing lacquer.
金属防水层的连接处要焊接,并涂刷防锈保护漆。
A thin layer of fusion zone is fused and compounded at the high tem" perature in explosion welding process."
在爆炸焊接的过程中,结合区一薄层基体金属,在高温下将发生熔化、熔解或化合。
Mutual information layer achieved communication between upper machine and welding machine by custom communication protocol.
信息交互层按照自己制定的协议实现上位机同焊机的通信。
It is strong and durable in use, meshed panel, bridge structure welding, bearing not gathering to one point. Loading per layer is 250kgs.
坚固耐用,层板呈网状,桥梁式结构焊接,受重不会集中在一点上,每层可负重250公斤。
During spot welding, length (l), position, range of under-fusion area of resinous layer and change of tissues, component near resinous layer are researched.
研究了在点焊过程中,中间树脂层未焊合区长度尺寸(L)、未焊合区所在部位、硬化区域大小、树脂层附近组织和成分的变化。
The welding tests show that the welding robot can make all-position and multiple-layer welds with high tracking accuracy, excellent quality and reliable behavior.
焊接工艺试验结果表明,焊接机器人自动跟踪精度高、焊缝质量好、工作稳定可靠。
The properties of the welded joint may be effectively enhanced by adopting neat multi-layer welding and technical welds.
多层焊和附加工艺焊缝是提高焊接接头性能的有效途径。
If the part needs to be welded subsequent to the oxidation treatment, the oxide layer must be removed before welding.
[nf - 14 d]倘若该零件需要在氧化处理后进行焊接,则焊接前必须将氧化层除掉。
Weld thermal cycle simulation was used to reproduce the structure in the HAZ of single run and multi-layer welding.
采用焊接热模拟再现了单道焊和多层焊haz的组织。
Weld thermal cycle simulation was used to reproduce the structure in the HAZ of single run and multi-layer welding.
采用焊接热模拟再现了单道焊和多层焊haz的组织。