With austenitic welding material, solid wire, flux-cored wire and electrode, welded joint mechanical property of TCS ferritic stainless steel all can meet usability.
T CS铁素体不锈钢采用奥氏体型焊材,实芯焊丝、药芯焊丝和电焊条方法,焊接接头力学性能可以满足使用要求。
We welded the high strength steel BIF340 in different spot welding processing parameters, the structure and property of the welding joint are analyzed.
采用不同的点焊工艺参数对高强度钢板BIF 340实施焊接,并对焊接接头进行组织性能分析,研究点焊参数对BIF 340焊接性能的影响。
The mechanical factors for the property of welding joint are welding defects, discontinuity of joint shape, welding residual stress and welding distortion.
通常,影响焊接接头性能的力学因素有焊接缺陷、接头形状的不连续性、焊接残余应力以及焊接变形。
Modification welding can slightly affect the joint tensile property, but can improve the weld surface quality and reduce the weld defects.
热处理工艺对接头的拉伸性能影响最大,能显著提高接头的抗拉强度;
Mechanical property and microstructure of T91 steel pipe joint with TIG welding on different high-temperature test process was researched.
采用不同的高温试验工艺对T91钢管的TIG焊接头进行处理,分析TIG焊接头在力学性能和显微组织上的差异。
The mechanical property of weld joint was tested and the microstructure was analysed, the welding process was proved feasible.
通过对焊接接头的力学性能检验、微观组织观察和分析,证明了该焊接工艺的可行性。
The composition of the welded joint obtained by the two welding methods are all uniform, the hardness is higher than the matrix metal, the comprehensive property is good.
两种焊接方法所得焊接接头成分均匀,硬度值均超过母材,综合性能良好。
Integrated influence of extrusion times and metal "s mechanical property to quality of cold pressure welding joint was discussed."
定性的讨论了挤压次数及材料力学性能对冷压焊接头性能的综合影响。
Integrated influence of extrusion times and metal "s mechanical property to quality of cold pressure welding joint was discussed."
定性的讨论了挤压次数及材料力学性能对冷压焊接头性能的综合影响。