The steel had low sensitivity to welding cold cracking.
结果表明，该钢具备较低的冷裂纹敏感性。
Measures were taken to prevent welding cold cracking such as improve welding technology by decreasing cooling speed and adopting low-hydrogen electrode, etc.
通过改进焊接工艺来降低冷却速度和采用低氢型焊条等措施来控制焊接冷裂纹的产生。
On the analysis of the mechanism of the tank welding cold cracking generation, specific methods to prevent cold cracking in tanks constructions are brought out.
文章分析了储罐焊接冷裂纹产生的机理，提出了在储罐施工中防止冷裂纹产生的具体措施。
The influence of Lanthanum, Cerium, Yttrium, Praseodymium and Neodymium on weld hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron was studied.
研究了纯镍铸铁焊条冷焊时，稀土金属镧、铈、镨、钇及钕对焊缝热裂纹敏感性的影响规律，并分析了铈对焊接接头力学性能和加工性能的影响。
The cold cracking sensibility of high tensile pipeline-steel was studied by Ygroove cracking test using seven kinds of high cellulose electrode of vertical down position welding.
采用七种高纤维素型立向下电焊条，通过斜y坡口裂纹实验，对高强管线钢的冷裂敏感性进行实验研究。
The proper interpass temperature is required to prevent cold and hot cracking as well as the proper selection of welding filler material, to produce the proper creep resistance and toughness.
需要适当的程间温度和正确选择填充金属材料来防止冷热裂缝，产生适当的蠕变阻力和韧性。
Neodymium can increase weld metal hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron.
纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。
A new low alloying steel with low susceptibility to weld cold cracking has been developed for large heat input welding in pressure vessel engineering.
试验结果表明，该钢具有焊接冷裂纹倾向低、可用大线能量焊接、焊后不宜进行消氢处理等特点，可用作高强度大焊接线能量用钢。
A new large heat input welding high strength low alloy steel with low susceptivity to weld cold cracking was developed and the cold strain aging behavior was investigated.
研制了一种低焊接裂纹敏感性高能量输入焊接用低合金高强钢，并研究了其冷应变时效行为。
A new large heat input welding high strength low alloy steel with low susceptivity to weld cold cracking was developed and the cold strain aging behavior was investigated.
研制了一种低焊接裂纹敏感性高能量输入焊接用低合金高强钢，并研究了其冷应变时效行为。