The change of weld depth and weld width is only related with current value but has little …
熔深和熔宽的改变只与电流的大小有密切关系,而电流方向对其影响不明显。
In addition, the changes of the laser pulse width and pulse frequency to affect the weld width were investigated.
此外,对激光脉冲宽度及脉冲频率对焊缝宽度的影响作了深入研究。
The paper researches the relation of parameters and weld width of TIG deposit surfacing used in rapid prototyping.
研究了用于快速成形的TIG熔敷堆焊工艺中各参数与焊缝宽度的关系。
Using this system and the analysis of the results, the relationship of weld parameters between weld width and weld height was gotten.
应用该系统进行了堆焊试验,对试验结果进行分析得出了焊接工艺参数与成型焊缝熔宽、余高之间的关系。
Weld-shape(butt weld width, size of fillet weld)is an indicator of weld features and it also is an important factor of quality welding.
焊缝尺寸 (如对接焊缝的焊缝宽度、角焊缝的焊角尺寸等 )是表示焊缝形状特征的指标 ,是影响焊缝质量的重要因素之一。
The paper clarifies some conservative views of the weld size concerned, theoretically analysing the dialectic relationship between the weld width, height and its quality.
本文澄清了人们对焊缝有关尺寸的偏见,从理论上分析了焊缝宽度、高度与焊接质量间的辨证关系。
Influence of the relative width of weld metal and strength of weld metal wes researched.
研究了焊缝金属相对宽度和焊缝金属强度对接头性能的影响。
Weld depth width ratio reaches 0.
焊缝深宽比达到0。
Cracks, growing at weld toe, tend to form at numerous sites along the transverse width perpendicular to the applied stresses.
焊趾处萌生的裂纹往往在垂直于作用应力方向沿着横向宽度在多处形成。
Based on these fuzzy control forms, weld pool width is easily controlled by adjusting welding current.
以焊接电流为控制量,可以根据此控制作用表对焊缝熔宽进行实时控制。
Sper-clean-up capacity of the oxide film to remove the width continuously adjustable, bright weld appearance.
超强清理氧化膜能力,清理宽度连续可调,焊缝光亮美观。
Its results show that with decreasing the relative width of under-matching weld metal, the tensile strength of welding joint increase.
结果表明:随低强焊缝金属相对宽度变小,接头抗拉强度增大;
The surface tension, arc blow force and electromagnetic force work positive to improve the penetration, and the buoyancy can increase the width in the middle of weld pool.
表面张力、电弧吹力和电磁搅拌力均有利于获得较大的熔深,浮力有利于增加焊缝中间部位的宽度。
With the increasing of heat input, the width of columnar crystal is increased, the dimension of acicular ferrite of weld metal is increased.
随着热输入增大,焊缝柱状晶宽度增大,焊缝中针状铁素体板条有粗化的趋势;
Control of the penetration and width of the back side weld was then achieved by controlling the width of an isothermal line near the melting point.
通过控制接近熔点温度的等温线宽度最终实现了对焊缝背面熔宽和熔透的控制。
A set of experimental measurement system to the chang process for impulse TIG welding pool width has been established based on contact measurement in front of weld by visual computers.
建立了一套以计算机视觉焊缝正面检测为基础的脉冲tig焊熔池宽度变化过程的实验检测系统。
The effective weld length for any groove weld, perpendicular or skewed to the direction of stress, shall be the width of the part joined.
垂直或斜交于应力方向的任何坡口焊缝的有效焊缝长度,应等于被连接部分的宽度。
The results show that the rational combination of welding parameters such as the laser power density, the welding speed, the pulse frequency and pulse width influence the quality of the weld beam.
焊接过程中合适的保护气体及其送气方式也是十分必要的。大量试验表明,激光功率密度、焊接速度、脉冲宽度和脉冲频率四个参数的合理组合是实现不锈钢薄板焊接的关键因素。
The transverse weld topography, the connect width between plates and tension and shear load were analyzed when the incident angle changed.
分析了入射角改变对焊接件外观形貌、焊缝截面、焊缝板间连接宽度以及所承受的拉剪载荷的影响。
The diffusion zone width of main alloying elements increases and hardness of the friction weld zone near TC4 titanium alloy side improves after post-weld heat treatment.
经焊后回火热处理后,主要合金元素沿焊合区的扩散区宽度增大;焊合区钛合金侧硬度值显著提高。
The diffusion zone width of main alloying elements increases and hardness of the friction weld zone near TC4 titanium alloy side improves after post-weld heat treatment.
经焊后回火热处理后,主要合金元素沿焊合区的扩散区宽度增大;焊合区钛合金侧硬度值显著提高。