It was found that the solidification cracking susceptibility of weld metal increases remarkably as nickel content increases.
结果表明：随着焊缝中含镍量的增加，焊缝金属的凝固裂纹敏感性增大。
In this paper, the temperature field of weld metal solidification cracking in the stainless steel was analyzed and simulated.
进行了不锈钢焊接凝固裂纹温度场分析与数值模拟。
Some plastic regions could be found and some dimples had been observed on the fracture surfaces of the solidification cracking of austenitic-ferritic weld metals.
少量铁素体的焊缝凝固裂纹断口上有许多小塑性区，有明显的韧窝。