This paper is a companion volume of "The wear failure analysis of phosphorus cast iron cylinder".
本文是“高磷铸铁汽缸套磨损失效分析”的姊妹篇。
This paper presents the application of wear particle analysis to the study of the effect of a particular factor (e. g. ionitriding temperature) on bearing failure.
本文介绍了磨损粒子分析在研究特殊因素(如离子氮化温度)对轴承失效的影响中的应用。
Through a number of statistical data analysis and further research to the failure gearing, the main problem in the usage of aero-bearing was corrosion and wear.
通过大量数据统计分析和失效轴承进一步研究，发现航空轴承使用中存在的主要问题是腐蚀和磨损。
Aimed at the wear problem of roll axle neck, failure analysis and rebuilding were made for multi-roller mill.
针对多辊筒碾压机压辊轴颈磨损严重的问题，对其进行了故障分析和改造。
A major limitation in our study was the variability inherent in using revision specimens for the analysis of covariate factors involved in the failure process and in the wear of the bearings.
我们研究的一个主要限制是我们都用翻修的病例来进行相关变量的分析，这些变量包括了手术的失败操作过程及磨损。
The qualitative study mainly includes experimental researches on influencing factors of wear resistance, failure types and mechanisms of the wear of the material and contact analysis.
定性研究主要是对该材料耐磨损性能的影响因素、磨损失效形式、磨损机理进行试验研究和接触分析。
In view of the work conditions of Dexing Copper Mine, the analysis of the wear failure of cone crusher was made.
根据德兴铜矿工况条件，对圆锥式破碎机衬板进行了磨损失效分析。
Simulating test and vibration signal analysis for abrasive wear failure of rollings bearings have been made in this paper.
对滚动轴承磨粒磨损故障进行了模拟试验和振动信号的处理和分析。
Failure analysis of high chromium cast iron liner has been studied by the microstructure, pole-pan wear abrasion, wet grinding and impact toughness.
用微观组织分析、杆盘式磨损、湿磨法磨损和冲击韧性等试验手段，对高铬铸铁衬板的显微组织、力学性能和耐磨性进行了试验分析。
Based on analysis of the process of pipe cold-drawing plug's wear-caused failure with the Dointview of friction science, measures for surface strengthening of the said plug were made.
用摩擦学的观点分析了冷拔顶头磨损失效过程，提出了冷拔顶头表面强化措施。
Based on analysis of the process of pipe cold-drawing plug's wear-caused failure with the Dointview of friction science, measures for surface strengthening of the said plug were made.
用摩擦学的观点分析了冷拔顶头磨损失效过程，提出了冷拔顶头表面强化措施。