Carried on the analysis to the lost wax casting craft sand hole defect creation factor.
对熔模铸造砂眼缺陷产生因素进行了分析。
Lost-wax casting: Traditional method of producing molds for metal sculpture and other castings.
蜡法：制作金属雕塑和其它铸件用的模具的传统方法。
The text detaily analyzes the cause of scab of stainless steel steel melt wax casting and proposes some measures to avoid it.
详细分析了不锈钢熔模铸件夹砂（起皮）产生的原因，并提出了防止不锈钢铸件夹砂（起皮）的一系列措施。
Lost wax casting, Die casting and mould, CNC machining, ductile and grey iron cast, stamping. powder coating, plating, e-casting.
铝合金压铸，压铸模具，精密铸造，精密加工，翻砂铸造，球墨铸铁，灰口铸铁，冲压件，电镀，喷塑，电泳…
Detailed analysis is done to the causes of while defects in lost wax casting. Some effective precautionary measures are proposed based on practical production.
对消失模铸造的铸件出现白色缺陷的原因进行了详细分析，并根据生产实际提出了一些有效的预防措施。
Precision injection molding, casting, mold repair metal jewelry and accessories, precision stampings, welding, lost wax castings, aluminum castings, stainless steel sand hole repair.
精密注塑、压铸、模具的修补金属饰品及配件、精密冲压件的焊接、失蜡铸件、铝铸件、不锈钢产品砂孔修补。
The positive can be produced either by direct modeling in wax over a prepared core (direct lost-wax casting), or by casting in a piece mold or flexible mold taken from a master cast.
正像可以用蜡直接在一个准备好的核心上浇铸成型(直接脱蜡浇铸)，也可以浇在一个模具中，或者从主铸件上取下来的柔韧的模具中。
A casting kit might include multiple casting compounds (dental gypsum, Silicone rubber), snow wax (for making a cast in snow), a bowl, a spatula and cardboard boxes to hold the casts.
铸模，一个碗，一个小铲和一个用于存放铸模的纸板盒。
Full-mold casting is a technique similar to investment casting, but instead of wax as the expendable material, polystyrene foam is used as the pattern.
实型铸造是与熔模铸造类似的技术，但它用做型模的消耗材料是聚苯乙烯泡沫而不是石蜡。
The art of carving wood, chiseling stone, casting or welding metal, molding clay or wax, etc. into three-dimensional representations, as statues, figures, forms, etc.
通过对木头、石头进行雕刻，对金属加以铸造、焊接，或对泥、蜡加工制成的三维雕塑作品。
By repeating technological tests and batch production tests for over a year, the fused silica was successfully used in the production of silica sol shell for low temperature wax precision casting.
经过反复的工艺试验及一年多批量生产验证，成功地将熔融石英应用于精铸用低温蜡—硅溶胶型壳生产中。
This paper introduces the process of making "nine dragon" tripod vessel and describes the technology and key for casting the body by lost wax pattern plaster mold process in detail.
前言：简述了“九龙鼎”的制作过程，详细介绍了用熔模石膏型铸造大型鼎身的工艺及要点。
Through the experiments and manufacture practice of wax setting and casting, some requirements for these procedures are probed.
通过蜡镶铸造工艺试验和生产实践，探讨了各环节的特殊工艺要求。
In wax setting and casting process, gemstones are pre-set in the wax models and directly set by the poured metal liquid solidifying.
首饰蜡镶铸造是将宝石预先镶嵌在蜡模中，铸造后金属液冷却收缩而直接将宝石固定在镶口中的工艺。
This paper introduces the making method of the strippable soft dies of handiworks and precision casting wax patterns which are made of the silicic rubber and PVC and its practical application.
介绍了用硅橡胶和聚氯乙烯两种材料制作工艺品及精铸蜡模的可剥软模具的制作方法及其实际应用。
One of the key-technologies of guiding device investment casting is getting internal ring, external ring and blade unit by splitting integral guiding device part for wax-mold design.
导向器类零件分体式精铸的关键技术之一是切分得到蜡模模具设计的内、外环及叶片单元体即如何实现分割面的生成。
Wax precision casting is adopted for the shaft sleeve, increasing material utilization ratio by 77% and realizing "less cutting and no cutting".
铸造工艺采用石蜡精铸成型，使材料利用率提高77％，达到少切削、不切削目的；
Key influential factor of causing the dimensional instability of wax pattern and casting for investment casting is the instability of component of reclaimed wax.
造成硅溶胶精铸蜡件与铸件不稳定的关键因素是回收蜡成分不稳定。
In the electronic ceramics thermal die-casting molding process, can improve the slurry viscosity, prevent body wax cracking.
在电子陶瓷热压铸成型工艺中，可提高料浆粘度，防止坯体排蜡开裂。
Hot pressure casting is usually used for the model of precision ceramics. Wax removing is a key process in production. Wax flowing out from the products is a common problem of the process.
前言：低压注射成型即热压铸成型工艺是精密陶瓷成型方法中较常见的一种工艺方法，其中成型后产品的脱蜡工序是整个生产工序中较重要的一个环节，在此环节中容易出现产品“流蜡” 缺陷。
Lin Chiao casting Co. Ltd. was established in 1988. We are expert for OEM in precision lost wax investment casting.
翎乔金属工业股份有限公司成立于1988年，为一专业OE M脱蜡铸造厂。
The processing procedure of prototype making by rapid prototype and the production process of cast steel box without wax pattern in investment casting were described.
给出了利用RP技术制造非金属原型的工艺流程，介绍了无模具熔模铸造箱体铸钢件的工艺过程。
The processing procedure of prototype making by rapid prototype and the production process of cast steel box without wax pattern in investment casting were described.
给出了利用RP技术制造非金属原型的工艺流程，介绍了无模具熔模铸造箱体铸钢件的工艺过程。