The influence of turbulence inhibitor on flow field in tundish has been studied by water modeling.
通过水力学模型实验，研究了中间包内流体流动的特性。
The distribution of fluid temperature in the tundish during plasma heating is investigated with water modeling.
采用水模在线加热研究等离子加热中间包流体温度的分布。
The influence of turbulence inhibitors with different structure on fluid flow behavior in tundish was studied by water modeling experiments.
通过水力学模型实验，研究了不同结构的湍流控制装置对中间包流体流动特性的影响。
The water modeling was performed by using two types of plastic particles as inclusions. The results show that the theoretical analysis is acceptable.
采用不同的模拟介质对中间包内夹杂物的去除做了研究，验证了理论分析的正确性。
In present study, a proposal to improve the inclusion floatation and temperature homogenization of molten steel is presented through an optimizing study by water modeling.
通过优化设计，提出了促进夹杂物上浮和均匀中间包内钢水温度的设计方案。
The effects of bottom blowing flow rate, top blowing flow rate and top lance level on mixed time in iron bath of smelting reduction furnace were studied with water modeling.
通过铁浴式熔融还原炉的水力学模型，实验研究了底吹流量、顶枪流量和顶枪枪位对熔融还原炉内混匀时间的影响。
And the surface velocity of molten metal in the mold was minimal at a magnetic flux density of 0.5 t, it agreed well with measured surface level fluctuations in water modeling.
施加0.5T的磁场使结晶器内金属液的表面流速最小，这一计算结果与实验结果十分吻合。
Based on the technology of rotating impeller DE gassing in aluminum alloy melt, the effect of pulse gas current on the gas bubble size by studied with the water modeling method.
在铝合金熔体净化旋转喷吹技术的基础上，采用水力模拟实验研究了脉冲进气方式对气泡大小的影响。
The effect of the ultrasonic stirring and gas stirring on the removal of inclusion was studied by the water modeling experiment under the condition of same unit stirring power in a container.
通过水模型实验，对同一容器内相同比搅拌功率条件下，超声搅拌和气体搅拌对去除夹杂物的影响进行了对比研究。
The characteristics of fluid flow in the mould of two ports SEN and four ports SEN have been compared and the influences of SEN on the level fluctuation are investigated by water modeling experiment.
比较研究了薄板坯连铸用二孔型水口和四孔型水口流场特征，水模试验结果表明，采用两种水口的薄板坯结晶器流场均存在非稳定性现象。
The water modeling of five - strand billet caster tundish was carried out. The result has showed the appropriate shape of flow control devices in tundish is feasible to improve flow pattern of fluid.
报导了五流方坯连铸中间罐内流体流动状态的水力学模拟试验研究，其试验结果表明：在该中间罐内设置适当的控流装置形式对改善中间罐内流体的流动模式是可行的。
Abstract: Water modeling of the six-strand caster tundish shows that the original design of the tundish can not meet the technical requirements for inclusion floatation and temperature homogenization.
文摘：通过水力学模拟六流连铸中间包后发现，原设计的中间包在夹杂物的上浮及温度的均匀性方面还存在不足，不能很好地满足生产工艺要求。
In order to reduce the inclusion quantity in the stainless steel slab, water-modeling experiment of stainless steel slab continuous casting tundish is launched.
为减少不锈钢连铸坯中夹杂物的数量，开展了不锈钢板坯连铸中包水模实验。
In order to reduce the inclusion quantity in the stainless steel slab, water-modeling experiment of stainless steel slab continuous casting tundish is launched.
为减少不锈钢连铸坯中夹杂物的数量，开展了不锈钢板坯连铸中包水模实验。