In this paper, research progress of the photo-initiators and their applications in UV curable adhesive were reviewed.
综述了光引发剂以及它们在紫外光固化粘合剂中的应用研究进展。
The influences of photoinitiator, crosslinking agent and cure time on the properties of UV curing pressure sensitive adhesive were discussed in the paper.
在常温下涂布后直接紫外光交联固化，考察了光引发剂、交联剂、光固化时间等因素对UV固化压敏胶综合性能的影响。
The optimal formula of the UV curable conductive adhesive gained from single factor test was as follows: Silver-plated copper powder 70%, complex photoinitiator 4%, AIBN 2% and KH570 2.5%.
通过单因素实验确定了导电胶的最佳配方：镀银铜粉填充量为70%、复合光引发剂用量为4%、热引发剂aibn用量为2%、偶联剂KH570用量为2.5%。
During encapsulation process, used optical photosensitive adhesive rapid solidification method under UV irradiation.
封装过程中，采用光学光敏胶紫外光照射下快速凝固法。
The results showed that the influence of UV light on adhesive property was great, and protection can slow the deterioration of adhesive strength of CFRP and concrete.
结果表明，紫外线对CFRP与混凝土的拉伸剪切强度影响较大，防护能有效缓减CFRP与混凝土的正拉粘结性能在紫外线作用下的劣化。
UV-curable adhesive monomer 10-methacryloyloxydecyl thiophosphoric acid dichloride was synthesized from the reaction of thiophosphoryl chloride with methylacrylic acid and 1,10-decanediol.
以甲基丙烯酸、1，10-癸二醇和三氯硫磷为主要原料合成出了紫外光固化粘接性单体10-甲基丙烯酰氧癸基硫磷酸二氯。
UV 574 is one component, high viscosity adhesive.
UV 574是一种单组分，高粘度粘接剂。
The effect of active monomers, oligomers and couple agent on shear strength and volume shrinkage of UV-curing adhesive was investigated.
考察了活性单体、预聚体及偶联剂对紫外光固化胶粘剂的粘接强度、体积收缩的影响。
This paper aimed at development of latent fingerprint on adhesive side of tapes and UV reflection photography was used.
目的研究胶带粘面上指印的提取方法。方法用短波紫外照相的方法对各种胶带粘面的指印进行拍照提取。
UV-curable adhesive is a class of important material that could be rapidly created adhesive bonding properties by the UV radiation.
紫外光固化胶粘剂是指借助UV辐射使粘接材料快速产生粘接性能的一类胶粘剂。
UV curing polyacrylate pressure sensitive adhesive was synthesized by core-shell polymerization, at the same time, chain transfer agent NDM was added for controlled reaction rate.
采用本体聚合方法将丙烯酸酯单体的混合物实施热聚合制备预聚体，采用核-壳聚合法的单体投料方式同时加入链转移剂十二烷基硫酵来控制反应进程。
Strong adhesive force: Crystal image appear snow, because between the film and UV glue lacks strong adhesive force, the film easy to tear.
超强黏合力：水晶影像出现雪花的主要原因，是由于胶片与UV胶水之间缺乏强有力的黏合，胶片很容易撕掉。
The invention relates to a novel method for preparing an anti-adhesive silicon coating on a base under short ultraviolet radiation (UV-C).
本发明涉及在短波紫外线(UV - C)辐射下在载体上制备有机硅防粘涂层的新方法。
The shear adhesive strength was characterized by universal tensile machine, and the adhesive mechanism of the mimetic polyurethane was also studied by UV-vis and rheology analysis.
通过万能电子拉力机测试了贻贝仿生聚氨酯的粘接性能，并通过紫外-可见光和流变行为测试初步探讨了粘接机理。
The shear adhesive strength was characterized by universal tensile machine, and the adhesive mechanism of the mimetic polyurethane was also studied by UV-vis and rheology analysis.
通过万能电子拉力机测试了贻贝仿生聚氨酯的粘接性能，并通过紫外-可见光和流变行为测试初步探讨了粘接机理。