The result shows that the inclusion, high cooling speed and uneven of cooling speed after rolling are the main reasons for steel plate cold bending rupture.
结果表明，钢板中有较多的非金属夹杂物及轧后冷却速度过快和冷速不均匀是导致冷弯性能不合格的主要原因。
Taking into account the rolling load is uneven, to balance electrical loads and reduce the electrical capacity slowdown in the increase between a flywheel and electric motors.
考虑到轧制负荷很不均匀，为了均衡电机负荷，减少电机的容量，在减速机和电动机之间加有飞轮。
Small deformation in high temperature is easy to cause incomplete recrystallization and bulky and uneven grain. It is hard to eliminate them in subsequent rolling process.
高温小变形时容易发生不完全再结晶，造成晶粒粗大且不均匀，在随后的轧制过程中很难消除。
Uneven deformation and extrusion drape in the different pass when rolling cause long strip defect on the surface. Defects on the surface and near surface are the main cause for cold heading to craze.
轧制过程中各道次的不均匀变形和挤压褶皱造成了圆钢表面的长条形缺陷，而表面和近表面缺陷是造成冷顶锻开裂的主要原因。
The main reasons of CSP work roll flaking in Lianyuan Steel are the uneven slab temperature, uneven roll cooling temperature and the rolling accident.
涟钢CSP工作辊发生剥落的主要原因是板坯温度不均、轧辊冷却温度不均和轧制事故。
The flow of metal in cast rolling area (liquid metal, sticky metal and solid shell) is an uneven medium flow.
铸轧区金属（液态金属、粘糊状金属和冷凝壳）的流动为非均匀介质流动。
The main reasons of CSP work roll flaking in Lianyuan Steel are the uneven slab temperature, uneven roll cooling temperature and the rolling accident.
介绍了在中厚板轧制中几种常见的工作辊剥落类型，联系实际分析其产生的原因，并提出了相关的预防措施。
The main reasons of CSP work roll flaking in Lianyuan Steel are the uneven slab temperature, uneven roll cooling temperature and the rolling accident.
介绍了在中厚板轧制中几种常见的工作辊剥落类型，联系实际分析其产生的原因，并提出了相关的预防措施。