Delamination and cause of polycarbonate (PC) thin-wall component were studied by comprehensive analysis methods and chemical stress cracking mechanism of PC delamination was found.
应用综合分析方法研究了聚碳酸酯(PC)薄壁件分层开裂及其起因，发现了分层的化学应力开裂机制。