This article provides a method to test corrosion speed of metal by resistance.
提供一种采用电阻法对金属的腐蚀速度进行检测的方法。
The present invention relates to one equipment to test corrosion resisting property of material by electrochemical process.
涉及一种用电化学方法测试材料耐蚀性能的装置。
Water vapor aging test whether experiment: discoloration or corrosion, and the subsequent spots solderability.
水蒸气老化实验:测试是否变色或腐蚀斑点,及后续的可焊性。
The corrosion behavior of GECM coupled with the LY12CZ aluminum alloy was also observed in immersion test.
同时对偶接了LY 12CZ铝合金的炭纤维环氧复合材料也进行了腐蚀浸泡对比试验。
The use of acid-base and humid environment on the corrosion of metal plating layer to test the corrosion resistance.
利用酸碱和湿热环境对金属的腐蚀性来测试电镀层的抗腐蚀能力。
To test stainless steel wire rope with different compositions immerged in seawater and to analyze and discuss anti-corrosion property.
对不同成分的不锈钢丝绳进行海水全浸试验,对耐腐蚀性能进行分析和讨论。
Contrast test simulating seawater has been performed on Marine pumps using SEBF sever corrosion prevention technology on the test bench in the Company.
采用SEBF重腐蚀防护技术的船用水泵,在公司内的试验台架上进行模拟海水的对比试验。
Soft PVC cemented with epoxy adhesives was used as the inside lining of the metal plate and its anti-corrosion performance was analyzed through the electrochemistry impedance test in this article.
利用环氧树脂胶粘剂粘结软质聚氯乙烯作为金属板材的内衬,通过电化学阻抗测试分析了聚氯乙烯内衬耐酸耐碱性能。
Corrosion resistance: salt test of plating, maybe according to the customers' needs, depend on the production, but at least 24 hours.
耐蚀性:阳极处理之盐雾测试,可依客户要求来规定,但至少要有24小时以上,视产品之定之。
The causes of the corrosion are investigated by galvanic corrosion test and system corrosion test and the protection measures are also proposed.
本文通过电偶腐蚀试验和系统腐蚀试验,查明了这种影响,并提出了防止钛合金对其它电位较负材料产生的电偶腐蚀作用的措施。
So, this paper made orthogonal corrosion test of multi-factor.
因此本文开展了多因素的正交腐蚀试验。
This test is used as a common method for expressing corrosion resistance of a coating system.
这种雾也可以是酸性的,这种试验是表述涂层耐腐蚀性能一个通用的方法。
The preparations before test shall include corrosion check, mechanical inspection, vehicle photo, coating thickness measurement, metal thickness identification, paint layer scratch and etc.
试验前的准备工作包括腐蚀检查、机械检查、车辆拍照、涂层厚度测量、金属厚度识别及油漆层划线等。
Objective The objective of this study was to test the corrosion resistance of Gallium alloy, a new mercury-free dental restorative material.
目的研究新型不含汞的牙体充填材料镓合金的抗腐蚀性能。
Chemical property testing: salt spray test of materials, corrosion test of stainless steel.
化学性能测试:材料的盐雾试验、不锈钢腐蚀试验等。
This article has described the structure, operation principle and test method of salt spray cabinet, and discussed various factors that influence the cycle corrosion test.
介绍了盐雾试验箱的构造,工作原理和试验方法,并探讨了涂层在循环腐蚀试验中的诸多影响因素。
The data of salt solution immersion test indicate that corrosion rate of aluminium alloy LY12 with ceria thin film is decreased.
盐水浸渍法试验结果证明了成膜后LY12铝合金表面的腐蚀速率明显降低;
Methods Verifying moisture content which caused the corrosion through the thermal storage test.
方法通过热储试验确定出现腐蚀的水分含量。
In chapter 4, according to the related standards and the particularity of the caustic medium, the paper puts forward a creationary laboratory metal corrosion test.
在第4章,参照相关标准,并根据腐蚀介质的特殊性,创造性的设计了试验室金属腐蚀试验。
The corrosion resistance of 07X16H6 precipitation hardening stainless steel in tempered state was studied using high temperature oxidation, salt-spray test and stress corrosion test.
通过高温抗氧化、盐雾腐蚀和应力腐蚀试验研究了07X16H6沉淀硬化不锈钢在使用状态(回火态)时的耐蚀性能。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
以45钢、A3钢、炮钢、20钢为金属试样,研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
Salt water with the concentration of 3% is used in the corrosion test for the samples welded under different laser parameters.
采用浓度为3%的盐水,对不同激光工艺参数的焊接件进行了腐蚀试验。
Corrosion test shows that proper rare earth addition enhance the general corrosion sensitivity.
腐蚀试验表明,添加微量稀土元素可增强抗点腐蚀敏感性。
Methods Suspended liquid quantitative sterilization test and metal corrosion test were carried out with different concentrations of disinfectant compound.
方法把消毒剂配制成不同浓度进行悬液定量杀菌试验及金属腐蚀试验。
The corrosion resistance of samples after passivation is studied in the experiment by humid-air accelerated corrosion test, nitric acid titrating test and the brine dipping test.
将黄铜片用上述三种溶液钝化处理后,通过湿热加速试验、硝酸点滴试验、盐水浸泡试验及电化学测试对耐腐蚀性进行了研究。
L-38 bearing shell corrosion test and 1g2 high temperature lustration engine stand test are carried out.
并进行L—38轴瓦腐蚀性和1g 2高温清净性发动机台架试验。
Usually, corrosion resistance of weathering steels is evaluated by the weight-loss method in an accelerated corrosion test.
通常利用加速腐蚀试验采用失重法表征耐候钢的耐大气腐蚀性能。
Through permeability resistance test, sulfate corrosion test and abrasion resistance test, the relationship of construction techniques, concrete surface quality and durability was reached.
通过混凝土抗渗性试验、抗硫酸盐腐蚀试验和耐磨性试验,得出施工工艺和混凝土表面质量与混凝土耐久性的关系。
The surface morphology progression of grey cast iron due to cavitation erosion induced by tap water has been studied carefully by cavitation corrosion test and SEM observation in turn.
采用空泡腐蚀与定位跟踪观察交替进行的方式,研究了灰口铸铁在自来水中空泡腐蚀过程的表面形貌演变。
The surface morphology progression of grey cast iron due to cavitation erosion induced by tap water has been studied carefully by cavitation corrosion test and SEM observation in turn.
采用空泡腐蚀与定位跟踪观察交替进行的方式,研究了灰口铸铁在自来水中空泡腐蚀过程的表面形貌演变。