The phase structure and microstructure of as-cast and quenched alloys were analyzed and observed by XRD and SEM.
用XRD和SEM分析了铸态及快淬态合金的相结构,并观察了合金的微观组织形貌。
The sensibility of the harden structure of high carbon steel to hydrogen and stress is researched through the tensile test of quenched specimens and charging hydrogen specimens after quenching.
利用高碳钢淬火试样及淬火后充氢试样的拉伸试验,研究了高碳钢淬硬组织对氢和应力的敏感性。
The effect of preheating treatment process of cold rolls on induction heat quenched structures and the effect of heating temperature and time on structure and hardness have been studied.
研究了轧辊的预备热处理工艺对感应加热淬火组织的影响,感应加热温度和时间对组织和硬度的影响。
The phase structure and microstructure morphologies of the as-cast and quenched alloys were analysed and observed by XRD and SEM.
用XRD和SEM分析了铸态及快淬态合金的相结构及微观组织形貌。
The structure, wear resistance and wear mechanism of laser quenched layer on the groove surface of the piston head were studied in this paper.
研究了大型柴油机活塞项环槽激光淬火层的组织、耐磨性和磨损机理。
The product is then quickly cooled or quenched to the desired extrusion temperature to prevent new precipitation of these phases in the alloy structure. Between the temperatures of 800. degree.
产品然后被快速冷却或淬火到期望的挤压温度,以防止这些相在合金组织中的新析出。
This dislocation cell structure is inherited by martensite, restricts the growing of the martensite and refines the structure so as to strengthen and toughen the magnetic field quenched materials.
高温顺磁性奥氏体在外强磁场的作用下可发生磁化变形,使奥氏体形成高密度的位错胞结构,并有弥散碳化物析出。
Uneven components of quenched martensite and residual austenite structure and improper grinding parameter are attributed to the main causes for cracks.
淬火组织中马氏体与残余奥氏体的成分不均匀及磨削用量参数选择不当是导致裂纹出现的主要原因。
Subroutines of non-quenched steel microstructure evolution are exploited, and structure property variable regular of non-quenched steel during RSM process is exploited.
开发了非调钢组织演变子程序,研究了非调钢在减定径机组轧制过程中组织性能的变化规律。
Subroutines of non-quenched steel microstructure evolution are exploited, and structure property variable regular of non-quenched steel during RSM process is exploited.
开发了非调钢组织演变子程序,研究了非调钢在减定径机组轧制过程中组织性能的变化规律。