The result shows that due to the reason of unsuitable control of the forging process, the forging fracture is in stone shape and the microstructure is extremely rough.
研究结果表明，锻材断口呈石状、显微组织枝晶特粗大的原因主要是由于锻造加热工艺控制不当造成。
The result shows that due to the reason of unsuitable control of the forging process, the forging fracture is in stone shape and the microstructure is extremely rough.
研究结果表明，锻材断口呈石状、显微组织枝晶特粗大的原因主要是由于锻造加热工艺控制不当造成。