The reaction current of oxygen evolution on lead was lower than that on lead-bismuth alloy at the same potentials in the anodic polarization curves.
阳极极化曲线测量表明，相同电位下，纯铅电极上的析氧电流稍小于铅铋合金电极上的析氧电流；
With the decrease of film thickness, the cathodic polarization current density of 7B04 Al-alloy increases, and the anode reaction is suppressed.
液膜厚度减小，7B04铝合金阴极极化电流密度增加，阳极反应受到抑制；
Both of the reaction were controlled by electro-chemical polarization.
两个放电步骤均受电化学极化控制。
The effects of SO2 concentration, H2SO4 concentration, temperature and stirring speed on anodic reaction rate were investigated using potentiostatic polarization measurement.
通过SO 2阳极极化曲线的测定，考察了SO2浓度、H2SO4浓度、温度和搅拌速度对阳极反应速率的影响。
The effects of SO2 concentration, H2SO4 concentration, temperature and stirring speed on anodic reaction rate were investigated using potentiostatic polarization measurement.
通过SO 2阳极极化曲线的测定，考察了SO2浓度、H2SO4浓度、温度和搅拌速度对阳极反应速率的影响。