The two concepts of slag blending ratio in cement and admixing quantity of slag are liable to be confused when producing cement with clinker powder and slag powder.
采用熟料粉、矿渣粉拌和水泥生产工艺，往往易混淆水泥中矿渣粉配比和矿渣掺入量这两个概念。
Reasonable slagging system could enhance the metallurgical properties of slag, the trouble could be solved that caused by slag quantity deceases; high quality hot metal could be produced.
采用合理的造渣制度可以使炉渣具有良好的冶金性能，解决渣量降低带来的问题，生产出高质量铁水。
In this paper, the influences of different agents, there addition quantity and particle size on the foaming performance of the refining slag with high basicity were investigated.
本文系统研究了发泡剂种类、加入量和粒度对高碱度精炼渣发泡效果的影响。
The compressive strength of cement is somewhat reduced with the increase of the slag quantity mixed, however, the soundness remains qualified.
水泥抗压强度随钢渣掺量的增加而有所降低，水泥安定性合格。
It was studied that the effect of the quantity of steel slag and silica fume on concrete strength and fluidity as well as the rule of the strength of concrete with steel slag and silica fume.
研究了钢渣、硅粉掺量对混凝土强度与流动性的影响以及钢渣、硅粉混凝土强度规律。
By mixing hardening agent HAS of different quantity with fly ash, stone bits and slag, some tests are carried out.
用不同掺量的HAS固化剂来固结粉煤灰、石屑及煤渣进行性能试验。
The slag grinding fineness, additives of exciting agent, modifier kind and quantity, which influence the dry contractibility and strength of slag cementing material, have been studied.
研究了矿渣的粉磨细度、激发剂的掺量、改性剂的种类与掺量对矿渣胶凝材料的干燥收缩性能及强度的影响。
The effects of cutting speed and aided oxygen pressure on the cutting quality and the adhesive slag quantity were analysed in the experiment of cutting of aluminium plate by CO2 laser.
在CO2激光切割铝面板的试验中，分析了切割速度和辅助氧压对切割质量及熔渣附着量的影响；解决了工件逆反射的难题；获得了激光切割铝板的较佳工艺参数。
With this model the EAF Steel-making process can be simulated, including of scrap melting procedure, the changes of temperature, slag quantity and compositions of steel, slag and off-gas.
该模型可动态地模拟电弧炉冶炼过程中的废钢量、炉温、渣量、钢液成分、炉渣组成和炉气成分的变化。
The effect of water binder ratio (W/C), slag binder ratio (S/C) as well as the adding quantity of steel fiber on cement based composite was studied;
研究了水灰比（W/C）、砂灰比（S/ C）、钢纤维掺量对水泥基复合材料性能的影响；
The crystallization behavior of anosovite in blast furnace slag was studied and the quantity of crystallization of anosovite in slag was measured at various conditions.
研究了含钛高炉渣中黑钛石的结晶规律及其晶体生长条件。
The crystallization behavior of anosovite in blast furnace slag was studied and the quantity of crystallization of anosovite in slag was measured at various conditions.
研究了含钛高炉渣中黑钛石的结晶规律及其晶体生长条件。