The corrosion mechanism of metallic components for aircraft and judgement process of corrosion grade were introduced.
介绍了飞机金属构件的腐蚀机理以及腐蚀等级的判断流程。
It also makes a theoretical and quantitative analysis of electrochemical process of corrosion in reinforcement of concrete.
对混凝土中钢筋锈蚀的电化学过程从理论上进行了定量分析和描述。
Reasons for pipeline corrosions are analyzed systematically and main types are summarized in the paper. Some problems occurred in the process of corrosion protection project are discussed.
系统分析了油库地下管路腐蚀的原因，总结出了管路腐蚀的主要类型，并对防腐工程实施中的一些具体问题进行了探讨。
This process produces corrosion of metals.
这一过程造成金属的腐蚀。
Strong erosion: the metal workpieces dip in with high and certain temperature erosion of solution, to remove metal workpieces surface oxides and corrosion things process.
强浸蚀：将金属制件浸在较高浓度和一定温度的浸蚀溶液中，以除去金属制件表面上氧化物和锈蚀物的过程。
Conversion of a metal surface to a less reactive state. A process to reduce corrosion rate of metal surfaces.
一种可以降低金属表面活性的转化膜，能够降低金属表面腐蚀几率的工艺。
The corrosion of reinforcing steel in concrete is an electrochemical process.
混凝土中钢筋的腐蚀是一个电化学过程。
Severe corrosion prevention for metal process pipelines of acid, base and salt.
酸、碱、盐等金属工艺管线的重腐蚀防护。
Plastic rockery stone stability is mainly rely on the main structure completed, but with the passage of time, steel in the process of contact with air and water, prone to corrosion and rust.
塑石假山的稳定性主要靠主结构来完成，但随着时间的推移，钢材在接触空气及水的过程中，容易发生腐蚀、生锈。
In the use process of the gas cylinder, if find any serious corrosion and damage or have doubts about its security, should be tested in advance.
气瓶在使用过程中，发现有严重腐蚀、损伤或对其安全性有怀疑时，应提前进行检验。
The process conditions of pretreatment, corrosion prevention coating, decorative coating and film's performance were studied.
研究了镁合金的前处理、防腐涂装以及装饰性涂装工艺条件及其涂膜性能。
This process was coincident with classic theory of crevice corrosion of metal.
这一过程与经典的金属缝隙腐蚀机理相吻合。
Scaling, corrosion and biological silt may be formed in usage process of circulation cooling water.
循环冷却水在使用的过程中，会在系统中产生结垢、腐蚀和生物粘泥。
The electrochemical corrosion process of iron in concentrated alkaline solution was discussed.
对铁在碱性溶液中的电化学腐蚀过程进行了讨论。
In the development and production process of oil and gas field, the impact of corrosion and damage is unpredictable.
在油气田的开发与生产过程中，腐蚀带来的影响和损失是不可预见的。
The technology for the corrosion diagnosis and reliability assessment is a systematic judgement process based upon the criterion established on the basis of the defined corrosion mechanisms.
对装置进行的腐蚀诊断、可靠性评估技术是以明确的腐蚀机理为基础建立起判据的一个系统判断过程。
The type, the characteristics, the formation process, and the influencing factors of filiform corrosion were analyzed and discussed.
对涂膜下铝合金丝状腐蚀的几个特点、类型、形成过程和影响因素进行了分析和讨论。
This paper introduces the corrosion and replacement of warm-water heater in decarbonization process and discusses the corrosion principle.
介绍了脱碳流程中温水加热器的腐蚀与更换，并对腐蚀的机理进行探讨。
Iron and steel parts with cracks are susceptible to corrosion in the site of cracks during electroplating process. Requisite options and preventive measures for crack corrosion were introduced.
带缝隙钢铁件在电镀与涂装过程中易发生缝隙腐蚀，介绍了缝隙腐蚀的产生条件及常用的预防措施。
While the chipping water applied in the process of circulation cooling water, the average corrosion velocity is 0.
切粒水回用于循环水冷却水系统过程中，腐蚀速率较高，平均为0。
The Chlorohydrin process produces large amount of wastewater, which results in serious equipment corrosion and environmental pollution.
氯醇法在生产过程中产生大量含氯废水，对环境造成严重污染。
The corrosion phenomenon of ionic membrane electrolyzer in production process was introduced. The reasons of corrosion were also discussed.
介绍了离子膜电解槽在生产运行过程中的腐蚀现象，讨论了产生腐蚀的原因。
The corrosion process of caustic liquid on carbon steel is introduced.
以碳钢为例，介绍了碱液的腐蚀过程。
Some causes of the Hydrogenization reactor that creates corrosion in the process of producing and running are discussed and its protective measures are raised in this paper.
本文分析了加氢反应器在生产运行过程中产生腐蚀的几种原因，并提出了防护措施。
The deposits obtained by the process has satisfactory appearance, corrosion resistance and hardness, and the plating bath has advantages of high covering power and current efficiency.
该工艺得到的镀层外观漂亮，防腐性和硬度较好，镀液覆盖能力强，电流效率高。
This article discusses the changes of corrosion potential and current for phosphating process of hard aluminium (LY12) in different conditions, namely, the growing process of phosphate coating.
讨论了硬铝(LY12)在不同条件下磷化过程中腐蚀电位和电流的变化，即磷化膜的生长过程。
In this paper, the corrosion mechanism of metal surface caused by air was proposed based on the principle of corrosion process of metal enclosed by the thin surface electrode.
本文以金属处于表面薄层电解质下的腐蚀过程为基础，提出大气对金属外表面腐蚀的机理。
In this paper the mechanism resulting in intergranular corrosion is described for 18-8 austenitic stainless steels. Some process factors of affecting the intergranular corrosion are analyzed as well.
本文叙述了18 - 8型奥氏体不锈钢中导致晶间腐蚀的机理，分析了影响晶间腐蚀成分和工艺方面的因素。
The process technologies, selection of equipment and its corrosion in the production of potassium sulphate from potassium chloride and ammonium sulphate are discussed.
提出以硫酸铵和氯化钾为原料，复分解制取农用硫酸钾的工艺条件及工艺流程，并探讨生产中设备选择及腐蚀问题。
The process technologies, selection of equipment and its corrosion in the production of potassium sulphate from potassium chloride and ammonium sulphate are discussed.
提出以硫酸铵和氯化钾为原料，复分解制取农用硫酸钾的工艺条件及工艺流程，并探讨生产中设备选择及腐蚀问题。