The process of using solid peroxide for producing special PP resin Z50S is described.
介绍了采用固体过氧化物生产聚丙烯专用树脂z50s的过程。
The melt index and ethylene content of clear PP resin for beverage bottles at home and abroad were analyzed.
剖析了国内外饮料瓶用透明聚丙烯熔体指数，乙烯含量。
The usage of PP resin pipe has been spread in this paper and its production and application have also been discussed here.
推广使用聚丙稀（PP）树脂管材，论述（PP）树脂管材的生产与应用。
This paper reviewed the developing prospect of spun - bond process PP resin exclusively for non - woven fabrics, and the current situation of Shanghai Petrochemical Co.
综述了纺粘法非织造布专用聚丙烯树脂的发展前景及上海石化利用有机过氧化物降解工艺开发生产纺粘法非织造布专用聚丙烯树脂(Y3700C)的现状。
This paper introduced the properties of polypropylene speciality HHP1 used for washing machine and analyzed the differences in properties of HHP 1 and general purpose PP resin.
分析了聚丙烯洗衣机内桶专用料HHP1的性能及其与通用料的区别；
Mixing modified agents, antioxidant, optical stabilizer, the special resin for water-supply pipes with pp C4220 as the base resin is developed.
以聚丙烯c 4220为基础树脂，加入适量改性剂、抗氧剂、光稳定剂，研制开发了给水管材专用料。
The speciality base resin of propylene random copolymer (PP - R) for tubing was successfully developed in the commercial plant through the study on the imported PP - R product.
通过对进口无规共聚聚丙烯（PP-R）产品的分析研究，在引进装置上成功生产出PP-R管材专用料的基础树脂；
The influences of basic resin, nucleating agents and its content, other agents, extrusion temperature and rotating velocity on the transparency of PP are studied by lab experiment.
小试研究了基础树脂、成核剂种类与含量、其它助剂及加工过程中挤出机温度与转速对PP透明性的影响。
Stabilization treatments of small bulk polypropylene( PP) resin were performed by using antioxidants and light stabilizers made in China.
选用国产抗氧剂和光稳定剂，对小本体聚丙烯树脂进行了稳定化试验。
The conditions for synthesis of PP (polypropylene) -diphenylcarbazide resin and separation and preconcentration of silver in geological samples have been studied.
研究了PP(聚丙烯)二苯氨基脲树脂的合成及其分离富集样品中银的条件。
Took PE as the carrier resin, joins foaming agent AC, nucleating agent and wrap agent, manufactured high performance foaming masterbatch which used for PP.
以PE作为载体树脂，加入发泡剂AC、成核剂、包覆体制备出高性能PP用微孔发泡母粒。
This paper studied the structure and properties of propylene-ethylene block copolymer (PP-B) as speciality resin for tubing.
研究了乙丙嵌段共聚聚丙烯(PP - B)管材专用树脂的结构与性能。
This paper introduced the development of speciality polypropylene (PP) resin TJ 1036 lor spinning, which was produced with the chemical degradation process.
介绍了用化学降解法生产聚丙烯纺丝专用树脂TJ 1036的开发过程。
A crystalline resin like pp has a white semi-opaque appearance due to the mixture of ordered and disordered domains, which bend light differently.
结晶性树脂如PP有白色的半透外观，这是由于存在有序和无序相区的混合物，它们对光的折射是不同的。
Using PP as matrix resin, POE as toughener, activated talc as reinforcer, compound for back cover of refrigerator compressor is prepared.
以聚丙烯为基料，POE为增韧剂，活化滑石粉为增强剂，研制出了冰箱压缩机后罩专用料。
The results showed that the extrudate with the most smooth surface was obtained when 5 phr of phenolic resin and 50/50 blending ratio of EPDM/PP were used.
结果表明，选择酚醛树脂硫化体系、控制酚醛树脂用量为5 份以及EPDM／PP共混比为50／50，可以得到挤出表面最为光滑的共混物。
By selecting material, process and designing of formula, a binder for PP-ink was prepared. Using this resin, the critical technical problem of peeling-off plastics ink is solved.
通过对原材料、工艺路线的选择以及配方的设计和筛选，研制出适用于聚丙烯塑料油墨用的粘连剂，解决了聚丙烯印刷油墨脱落的关键技术难题。
The results showed that it was better for producing the EPDM/PP TPV by selecting a high molecular weight resin, a suitable crosslinking system and optimum mixing conditions.
结果表明：在橡塑表面能相近的条件下，选择分子量大且结晶度高的PP作为基体组分，同时选择具有适宜交联速率硫化体系作为橡胶相的交联组分制备的TPV性能最佳。
A one coat paint based on this modified resin has been formulated, which shows good comprehensive properties and find applications for PP plastic parts in cars, etc.
然而聚丙烯塑料本身极性低，结晶化程度高，要形成具有良好附着力的涂层相当困难。
A one coat paint based on this modified resin has been formulated, which shows good comprehensive properties and find applications for PP plastic parts in cars, etc.
然而聚丙烯塑料本身极性低，结晶化程度高，要形成具有良好附着力的涂层相当困难。